Effect of Modification Treatment for Reduction of Dephosphorization Slag in Hot Metal Bath |
JIANG Mao-fa,CUI Yu-yuan,WANG De-yong,MIN Yi,LIU Cheng-jun |
Institute of Ferrous Metallurgy, School of Materials and Metallurgy, Northeastern University,Shenyang 110004, Liaoning, China |
|
|
Abstract To extract the valuable elements from the steel slag, a novel approach has been proposed by modification treatment to provide the stronger driving forces and accelerate the reduction. Three types of dephosphorization steel slags were reduced using carbon-saturated iron bath to extract iron and phosphorus simultaneously. During the process of reduction, slag composition, temperature, and original P2O5 content were investigated respectively. Slag modification treatment, adding either silica or alumina to vary the slag composition, was proven to accelerate the reduction of dephosphorization slag. The equilibrium time can be shortened from 60 to 30 min. Slag modification also allowed the reduction reaction to occur at lower temperature. After slag modification, the original P2O5 content in slag presents a slight difference on reduction process. Almost half of the reduced phosphorus was vaporized within 5 and 20 min. As more and more FeO was reduced, CO gas generation decreased, and evaporation amount of phosphorus therefore decreases.
|
Received: 19 January 2012
Published: 31 January 2013
|
Corresponding Authors:
Wang Deyong
E-mail: deyong_wang@163.com
|
|
|
|
[1] |
GUO Yu- feng,,GUO Xing- min. Effect of MgO on low temperature reduction process of hematite fines sinter[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 697-703. |
[2] |
GUO Pei-min��ZHAO Pei��WANG Lei��KONG Ling-bing. Oxidizing kinetics of reducing gas during iron oxide reduction process[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 22-26. |
[3] |
XU Cong-min,ZHANG Xuan,LUO Li-hui,YANG Dong-ping. Corrosion behavior of X100 pipeline steel in near neutral pH soil solution with action of SRB[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 562-569. |
[4] |
CHU Man-sheng��TANG Jue��LIU Zheng-gen��YING Zi-wei. Present situation and progress of comprehensive utilization for high-chromium vanadium-bearing titanomagnetie[J]. Chinese Journal of Iron and Steel, 2017, 29(5): 335-344. |
[5] |
ZHANG Hong-liang����SHI Qi��LONG Hong-ming����LI Jia-xin��CHUN Tie-jun��GAO Zhi-fang. Analysis of [NOx]removal process in sintering flue gas[J]. Chinese Journal of Iron and Steel, 2017, 52(5): 100-106. |
[6] |
DONG Wen-liang��LUO Lei��TIAN Zhi-hong��JI Chen-xi��LIU Yan-qiang��PAN Hong-wei. Recycle of decarburization-slag in dephosphorization-furnace of duplex process in converter[J]. Chinese Journal of Iron and Steel, 2017, 52(5): 36-42. |
|
|
|
|