| Direct Reduction Experiment on Iron-Bearing Waste Slag |
| CHENG Xiang-li,ZHAO Kai,QI Yuan-hong,SHI Xue-feng,ZHEN Chang-liang |
| State Key Laboratory of Advanced Steel Process and Products, Central Iron and Steel Research Institute, Beijing 100081, China |
|
|
|
|
Abstract A lot of iron-bearing slags were produced, and whose grade is much more than that of industrial iron ore grade. Chemical analysis and phase identification shows that the iron-bearing slag is amorphous, has fayalite main phase, iron grade is 36. 10%, and is difficult to recover iron from the slag. Thermodynamic calculation indicates that CO cannot reduce fayalite at high temperature and carbon direct reduction can be effective. Moreover, the reaction begins at 770 �� and the temperature can be reduced down to 500�� when CaO is added. On this basis, a method is put forward to making direct enrichment of iron by taking carbon contained pellets to realize the rapid reduction of fayalite, and the direct reduction process were studied in this paper. Experiments show that xC/xO should be less than 1. 5 for the need of reduction and carburization, and CaO and Al2O3 can spur the reduction of fayalite. On conditions that xC/xO is 1. 2, metallization rate can be 77% when temperature is 1250 �� and only carbon is added, and metallization rate can be 74% when temperature is 1200 �� and only CaO is added. Moreover the addition of Al2O3 can get a higher metallization rate (10% or so) than usual as R is between 0. 4 and 1. 0. Under the optimized condition of R equals to 0. 6, temperature of 1250 ��, slag melting point of 1320 ��, and time of 30 min, the metallization rate can reach 88. 43%.
|
|
Received: 18 January 2012
Published: 02 April 2013
|
|
|
|
| [1] |
ZHOU Li,LIANG Jian,WANG Xiang- hong,ZHANG Ping,SHI Xiao- fang. Effect of refining slag with different basicities and low alumina content on inclusion composition of spring steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 626-636. |
| [2] |
LI Jie��XIN Zi-cheng��YANG Ai-min��ZHANG Yu-zhu��LIU Lian-ji��SONG Ya-xian. Effect of basicity on quality of magnesium fluxed pellets[J]. Chinese Journal of Iron and Steel, 2017, 52(7): 35-41. |
| [3] |
PAN Xiao-liang,LI Jin-yan,GUO Min,ZHANG Mei. Effects of binary basicity and Al2O3 on phosphate enrichment in CaO-SiO2-FeO-Fe2O3-P2O5-Al2O3-MgO-MnO slag[J]. Chinese Journal of Iron and Steel, 2017, 29(6): 474-480. |
| [4] |
MA Shuai����LI Yu����ZHANG Ling-ling��LU Xiang����CANG Da-qiang��. Effects of EAF slag basicity on its recovery rate of iron components[J]. Chinese Journal of Iron and Steel, 2017, 52(4): 78-83. |
| [5] |
ZHOU Zhi-qiang��ZHU Zi-zong��DING Yu-chuan��ZHOU Sheng-nan. Effect of Na2O on dephosphorization for high phosphorus SiMn alloys[J]. Chinese Journal of Iron and Steel, 2017, 52(4): 13-17. |
| [6] |
ZHAI Jun,,LI Jian-min,,,LANG Wei-yun,LIU Liu. Effect of LF refining slag basicity on composition of inclusions in 304 stainless steel[J]. Chinese Journal of Iron and Steel, 2017, 29(2): 117-122. |
|
|
|
|
2013, Vol. 20 