| Heat Transfer During Quenching by Plate Roller Quenching Machine |
| WANG Chao1,WANG Zhao-dong1,YUAN Guo1,WANG Dao-yuan2,WU Jun-ping2,WANG Guo-dong1 |
1. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819,Liaoning, China
2. Nanjing Iron and Steel Co. , Ltd. , Nanjing 210035, Jiangsu, China |
|
|
|
|
Abstract For plate quenching on a roller quenching machine, heat transfer process is investigated. According to the practical online experiment of plate center temperature, average heat transfer coefficient under different conditions and temperature fields are analyzed by numerical simulation. The results show that, at the water temperature of 15 ��, the instantaneous maximum quenching cooling rate is 17. 6 ��/s for the plate of 50 mm in thickness in roller quenching process. In the temperature range of 400-850 ��, the maximum is 12. 1 ��/s. With the plate surface temperature decreasing, surface heat transfer coefficient increases at first, and reaches the maximum value of about 15000 W/(m2��K), and then decreases. The calculated heat transfer coefficients are applied to analyze plate temperature field of different thicknesses, and the difference between the calculated and measured temperature is less than 5%.
|
|
Received: 04 November 2011
Published: 15 May 2013
|
| Fund:Item Sponsored by National Basic Research Program of China |
|
Corresponding Authors:
WANG Chao
E-mail: ral_wangchao@163.com
|
|
|
|
| [1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
| [2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
| [3] |
JIANG Zhou-hua��ZHANG Xin-fa��LIU Fu-bin��GONG Wei. Harmful impurities control of raw material used in Ni-based superalloy production[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 1-10. |
| [4] |
SONG Guang-yi��YANG Quan��WANG Xiao-chen��ZHANG Xi-bang�� WANG Feng-mei��WANG Qiu-na. Work roll wear law for hot strip temper mill[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 54-59. |
| [5] |
WANG Bing-xing��XIONG Lei��ZHANG Tian��WANG Zhao-dong��WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 60-65. |
| [6] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
|
|
|
|
2013, Vol. 20 