| Effect of Modification Treatment on Inclusions in 430 Stainless Steel by Mg-Al Alloys |
| JIANG Zhou-hua,ZHUANG Ying,LI Yang,LI Shuang-jiang |
| School of Materials and Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
|
|
Abstract Refining process of 430 stainless steel in AOD (argon oxygen decarburization) was simulated under the experimental condition. Al was chosen as deoxidizer, Mg-Al alloy was added in process of refining, and slag used in oxidation period of AOD was chosen in the experiments. The variation of total oxygen content, the size, morphology and composition of inclusions in refining process and the mechanical properties, pitting corrosion resistance of final samples were studied. The results show that no obvious differences in total oxygen content were observed among all the experiments. Neither chain nor cluster Al2O3 inclusions were found in refining process of experiments treated by Mg-Al alloys, the average size of inclusions in the steel treated by Mg-Al alloys was less than that of inclusions in steel not treated by Mg-Al alloy. 430 stainless steel treated by Mg-Al alloy shows better tensile strength, yield strength, and pitting resistance than that in the contrast experiment.
|
|
Received: 06 January 2012
Published: 15 May 2013
|
|
Corresponding Authors:
Shuang-jiang Li
E-mail: two_river@yahoo.cn
|
|
|
|
| [1] |
Qiong XIE,Pei-yang SHI,Cheng-jun LIU,Mao-fa JIANG. Effects of Different Oxidants on HCl-based Pickling Process of 430 Stainless Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 778-783. |
| [2] |
WANG Hai-ren,,JIANG Yan,QU Jun-e,CAO Zhi-yong,LIU Shao-bo,GUO Xing-peng. Adsorption and Corrosion Inhibition Performances of 1-Tetradecylphosphonic Acid Self-Assembled Monolayers on 430 Stainless Steel Surface[J]. Chinese Journal of Iron and Steel, 2013, 20(9): 93-98. |
| [3] |
ZHAO Hai-quan,,QI Yuan-hong,SHI Yong-lin,NA Xian-zhao,FENG Huan-lin. Mechanism and Prevention of Disintegration of AOD Stainless Steel Slag[J]. Chinese Journal of Iron and Steel, 2013, 20(4): 26-30. |
| [4] |
WANG Hai-ren,,XIAO Zhen,QU Jun-e,YANG Hong-wei,CAO Zhi-yong,GUO Xing-peng. A Comparison Study on Corrosion Resistance of 430 Stainless Steel Surfaces Modified by Alkylsilane and Fluoroalkylsilane SAMs[J]. Chinese Journal of Iron and Steel, 2013, 20(12): 75-81. |
| [5] |
JIANG Mao-fa,CUI Yu-yuan,WANG De-yong,MIN Yi,LIU Cheng-jun. Effect of Modification Treatment for Reduction of Dephosphorization Slag in Hot Metal Bath[J]. Chinese Journal of Iron and Steel, 2013, 20(1): 1-6. |
| [6] |
JIANG Mao-fa,CUI Yu-yuan,WANG De-yong,MIN Yi,LIU Cheng-jun. Effect of Modification Treatment for Reduction of Dephosphorization Slag in Hot Metal Bath[J]. Chinese Journal of Iron and Steel, 2012, 19(3): 1-6. |
|
|
|
|
2013, Vol. 20 