| Melting Characteristics and Wettability of Binding Phase in Sinter |
| SHEN Feng-man,LI Guang-sen,DING Zhi-min,MU Lin |
| School of Materials and Metallurgy, Northeastern University, Shenyang 110004, Liaoning, China |
|
|
|
|
Abstract The melting characteristics and wettability of the binding phase in high basicity sinter were studied. By changing nCaO��nFe2O3 (molar ratio of CaO to Fe2O3) as well as the percentage of MgO, SiO2, and Al2O3, the melting characteristics and wettability of the binding phase were discussed. The results indicated that the characteristic melting temperature was the lowest and wettability was the best at nCaO��nFe2O3=1��1 (without addition); the addition of MgO increased the characteristic melting temperature and contact angles; when the percentage of SiO2 or Al2O3 was 3%, the characteristic melting temperature was the lowest, whereas the contact angles increased with an increase in SiO2 and Al2O3 contents.
|
|
|
|
|
|
| [1] |
Yuan-dong Pei,,,Sheng-li Wu,,Shao-guo Chen,Zhi-xing Zhao,Gang An,Zheng-ming Cheng, Yao-sheng Luo. Sintering of solid waste generated in iron and steel manufacturing process in Shougang Jingtang[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 697-704. |
| [2] |
Shi-feng Liu,,*,An Li,Yao-jia Ren,Dong-feng Li,Zhao-hui Zhang. Heat transfer performance of porous titanium[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 556-560. |
| [3] |
Wen-juan Ge,Xu-ting Li,Peng Li,Peng-chao Qiao,Jian-wei Du,Shuai Xu,Yan Wang*. Microstructures and properties of CuZrAl and CuZrAlTi medium entropy alloys prepared by mechanical alloying and spark plasma sintering[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 448-454. |
| [4] |
Shan Ren*,Fu-qiang Guo,Qi Zhao,Jie Yang,Lu Yao,Ming Kong. Sintering flue gas desulfurization with different carbon materials modified by microwave irradiation[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 979-984. |
| [5] |
Cong-cong Yang,,De-qing Zhu,Ben-jing Shi,Jian Pan,Li-ming Lu,Xiao-bo Li,Ya-ping Mo. Comparison of sintering performance of typical specular hematite ores with distinct size distributions[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 1007-1015. |
| [6] |
Wei Wang,,Ming Deng,,Run-sheng Xu,,Wei-bo Xu,,Ze-lin Ouyang,,Xiao-bo Huang,,Zheng-liang Xue,. Three-dimensional structure and micro-mechanical properties of iron ore sinter[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 998-1006. |
|
|
|
|
2009, Vol. 16 