Thermodynamic Model for Calculating Activity of Nitrogen and Boron in Fe-C-B-N Molten Metal |
WANG Shi-jun1,PENG Jun1,2,DONG Yuan-chi1,LIU Li-xia1,ZHOU Yun1,CHEN Er-bao1 |
1. School of Metallurgy and Resource, Anhui University of Technology, Ma′anshan 243002, Anhui, China
2. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract The solubility of nitrogen in Fe-C-B-N system was measured at 1 758 K, and the computational model on activity (action concentration) of nitrogen and boron was established based on phase diagram and the coexistence theory about metal melt structure model. Comparing the computed results with the experimental results, satisfactory conclusion can be obtained. The result shows that BN and B4C can exist in Fe-C-B-N molten metal at high temperature, which consequently restrains the nitrogen removal from the melt. However, B4C content is extremely low. Before graphite is precipitated, the influence of carbon on activity of nitrogen in melt is higher in ternary system than in binary system; however, this effect is contrary to that after graphite is precipitated.
|
|
|
|
|
[1] |
Hua��qiang HAO,,Yu��zhu ZHANG,,Su��ju HAO,Chao��fa ZHANG,Wu��feng JIANG,Peng��hui CUI. Preparation and Metallurgical Analysis of High Activity Burnt Lime for Steelmaking[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 884-890. |
[2] |
ANG,,Yan-ping BAO,. e and Control of Nitrogen for X70 Pipeline Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(7): 647-654. |
[3] |
Ya-yu LI,Zhen-nan LIU,Dong-ping TAO. An Estimation of Component Activity of Vanadium-bearing Liquid Iron and Transition Temperature of Vanadium Oxidization Using MIVM[J]. Chinese Journal of Iron and Steel, 2015, 22(7): 557-565. |
[4] |
Lei GAN,,Hai-feng WANG,Xiu-ping LI,Yuan-hong QI,Chun-xia ZHANG. Strength Activity Index of Air Quenched Basic Oxygen Furnace Steel Slag[J]. Chinese Journal of Iron and Steel, 2015, 22(3): 219-225. |
[5] |
Sheng-fu ZHANG, Liang-ying WEN, Kun WANG, Chong ZOU, Jian XU. Effects of Additives on Sulfur Transformation, Crystallite Structure and Properties of Coke during Coking of High-sulfur Coal[J]. Chinese Journal of Iron and Steel, 2015, 22(10): 897-904. |
[6] |
Guo-hua ZHANG,, Kuo-chih CHOU,. Deoxidation of Molten Steel by Aluminum[J]. Chinese Journal of Iron and Steel, 2015, 22(10): 905-908. |
|
|
|
|