| Strain Hardening and Strain Rate Sensitivity Behaviors of Advanced High Strength Steels |
| F Ozturk1,A Polat1,S Toros1,R C Picu2 |
1. Department of Mechanical Engineering, Nigde University, Nigde 51245, Turkey
2. Department of Mechanical,Aerospace and Nuclear Engineering, Rensselaer Polytechnic Institute, Troy 12180, New York, USA |
|
|
|
|
Abstract The mechanical properties of commercial dual phase (DP), transformation induced plasticity (TRIP), and high strength low alloy (HSLA-340) steel sheets are investigated and compared at various strain rates ranging from 0. 0017 to 0. 17 s-1 at ambient temperature. TRIP steel outperforms the other two materials, having comparable ductility and twice as large strength relative to DP steel. TRIP has larger strength and much larger ductility than HSLA-340. The exceuent ductility of TRIP800 is due to its high strain hardening capability, which promotes stable plastic deformation. It is observed that the strain hardening rate in TRIP800 does not decrease to zero at failure, as common in most materials in which failure is preceded by necking.
|
|
Received: 27 September 2011
Published: 18 June 2013
|
|
|
|
| [1] |
Hai-yan Tang*,Yong Wang,Guang-hui Wu,Peng Lan,Jia-quan Zhang. Inclusion evolution in 50CrVA spring steel by optimization of refining slag[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 879-887. |
| [2] |
H. Gonzalez,J.A. Ramos-Banderas,E. Torres-Alonso,G. Solorio-Diaz,C.A. Hern��ndez-Bocanegra,. Multiphase modeling of fluid dynamic in ladle steel operations under non-isothermal conditions[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 888-900. |
| [3] |
Zong-ye Ding,Di Zhang,Qiao-dan Hu,,*,Long Zeng,Jian-guo Li,. Constitutive analysis and optimization on hot working parameters of as-cast high Cr ultra-super-critical rotor steel with columnar grains[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 916-924. |
| [4] |
Hao Li,Yan-chong Yu,,Xiang Ren,Shao-hua Zhang,She-bin Wang,,*. Evolution of Al2O3 inclusions by cerium treatment in low carbon high manganese steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 925-934. |
| [5] |
Yu-cheng Lei,,*,Xiao-kai Guo,Hong-xia Chang,Tian-qing Li,,Qiang Zhu,Gang Chen, Long-ren Xiao. Cavitation erosion behavior of CLAM steel weld joint in liquid lead-bismuth eutectic alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 935-942. |
| [6] |
Zhen Cao,Shu-qi Wang*,Ke-zhi Huang,Bo Zhang,Guo-hong Wen,Qiu-yang Zhang,Lan Wang. Effect of artificial tribological layer on sliding wear behavior of H13 steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 943-949. |
|
|
|
|
2013, Vol. 20 