| Solid-Phase Decarburization of High-Carbon Ferromanganese Powders by Microwave Heating |
| GUO Li-na1,CHEN Jin1,SHI Wen-li1,ZHAO Jing1,LIU Ke2,LIU Jin-ying3 |
1. College of Materials Science and Engineering, Taiyuan University of Technology, Taiyuan 030024,Shanxi, China
2. Lian-zhi Technology Corporation of Xiangtan City, Xiangtan 411101, Hunan, China
3. No��12 Research Institute, China Electronics Technology Group Corporation, Beijing 100016, China |
|
|
|
|
Abstract The solid-phase decarburization of high-carbon ferromanganese powders (HCFPs) was investigated using calcium carbonate as the decarburizer by microwave heating and conventional heating methods to explore the differences of microwave heating and conventional heating. Experimental results show that HCFPs containing calcium carbonate were heated up to 900, 1000, 1100, and 1200 �� and held for 60 min for decarburization by microwave heating at decarburization ratios of 76��69%, 82��90%, 84��11%, and 85��75%, respectively. These ratios are higher than the decarburization ratios used for conventional heating under the same experimental conditions. The microwave heating can significantly improve decarburization ratio. This indicates the microwave heating field features a non-thermal effect, which in turn, visibly enhances the carbon diffusion ability of HCFPs. It also improves the kinetic conditions of solid-phase decarburization.
|
|
Received: 03 February 2012
Published: 23 August 2013
|
|
|
|
| [1] |
WANG Yi-ci,LI Hai-yang,LUO Guo-ping,LI Shuang-wei. Macrokinetics of gasification dephosphorization of converter slag by microwave carbon thermal reduction[J]. Chinese Journal of Iron and Steel, 2017, 29(2): 93-97. |
| [2] |
WANG Yi- ci,LI Hai- yang,LI Shuang- wei,LUO Guo- ping. Thermodynamic analysis and experiment on gasification dephosphorization reaction of converter slag[J]. Chinese Journal of Iron and Steel, 2016, 28(6): 31-34. |
| [3] |
CHEN Yan,BAI Chen- guang,YOSHIKAWA Noboru,TANIGUCHI Shoji. Numerical simulation on the heating of blast furnace (BF) slag with high TiO2 under microwave irradiation[J]. Chinese Journal of Iron and Steel, 2016, 28(2): 14-18. |
| [4] |
HU Bing,,HUANG Zhu-cheng,WANG Zhao-cai,,SUN Ying,. Microscopic mechanism of oxidized pellets during coal-based direct reduction by microwave heating[J]. Chinese Journal of Iron and Steel, 2016, 28(10): 43-49. |
| [5] |
AI Li-qun, ZHANG Xiao-mei, ZHANG Yan-long, HONG Lu-kuo. Lime activity and microstructure by microwave heating[J]. Chinese Journal of Iron and Steel, 2015, 50(1): 76-80. |
| [6] |
JIA Jing-yan,ZHU Hong-bo,PENG Jin-hui,ZHANG Li-bo,ZHOU Jun-wen,YANG Kun. Research of Reducing Ilmenite by Combined Reducing Agent Under Microwave Heating[J]. Chinese Journal of Iron and Steel, 2014, 26(9): 14-18. |
|
|
|
|
2013, Vol. 20 