| Corrosion Behavior of Different Steel Substrates Coupled With Conductive Polymer Under Different Serving Conditions |
| LIU Xiao-hei,XIA Zhi-dong,ZHOU Hu,YUAN Bo,LI Zhe,GUO Fu |
| College of Materials Science and Engineering, Beijing University of Technology, Beijing 100124, China |
|
|
|
|
Abstract The corrosion behaviors of stainless steel and nickel-plated carbon steel coupled with conductive polymer were investigated in both hot humid environment and simulated marine environment. The corrosion currents of different steel substrates and conductive polymer in simulated marine environment at room temperature were measured. The corrosion surfaces of different steel couples were observed under a scanning electron microscope (SEM) and chemical compositions were examined by energy dispersive spectrum (EDS) analysis. The corrosion mechanism was discussed. The results showed that the stability of both stainless steel and nickel-plated carbon steel in hot humid environment was excellent and no corrosion happened in the blank test for 360 h while slight corrosion existed in the contact area of coupled steel substrates. In simulated marine environment, the corrosion current of the stainless steel was lower than 100 ��A and some directional rod-like particles formed on the surface of the stainless steel, which are mainly caused by oxidative corrosion among different phases. The corrosion current of the nickel-plated carbon steel couples was much greater than that of stainless steel couples and nickel plate cracking resulted in the corrosion of the internal iron because the coated nickel layer was not dense enough.
|
|
Received: 05 April 2012
Published: 23 August 2013
|
| Fund:the special funds of Chaoyang District and Motorola |
|
|
|
| [1] |
XU Ying����ZHANG Zi-zi����WANG Bian����HU Chen-guang����WANG Huan-huan��. Curing influence factors and mechanism of stainless steel slag in AOD[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 43-47. |
| [2] |
LEI Dong��REN Yong��CHENG Xiao-ru��LAN Kun��QIU Jun��HUANG Da-jun. Effect of heat treatment on microstructure and mechanical properties of 316L/Q235 stainless steel composite panel[J]. Chinese Journal of Iron and Steel, 2017, 52(5): 66-71. |
| [3] |
LIU Bao-long����ZHANG Hui-fang��XIAO Zhen-xing��[LU]Zhi-qing��FU Wan-tang��REN Ting-zhi. Microstructure evolution and properties of interface in 316L/Q345R hot rolled clad plate[J]. Chinese Journal of Iron and Steel, 2017, 52(5): 72-76. |
| [4] |
WANG Li-ying. Influence of the high temperature aging on the microstructure and mechanical properties of 441 stainless steel[J]. Chinese Journal of Iron and Steel, 2017, 35(5): 15-19. |
| [5] |
CHEN Lei����ZHANG Ying-jie��LI Fei��PEI Jian-ming��SONG Lei-jun��JIN Miao. Effect of solution temperature on TRIP/TWIP behavior of a lean duplex stainless steel[J]. Chinese Journal of Iron and Steel, 2017, 52(4): 55-60. |
| [6] |
QI Qi-song����XU An-jun����HE Dong-feng����PAN Jiang-tao��. Carbothermic reduction for recycling of iron and chromium from stainless steel slag[J]. Chinese Journal of Iron and Steel, 2017, 52(3): 82-87. |
|
|
|
|
2013, Vol. 20 