| Mechanism of Black Strips Generated on Surface of CSP Hot-Rolled Silicon Steel |
| LIU Xiao-jiang,CAO Guang-ming,NIE Da-ming,LIU Zhen-yu |
| State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
|
|
Abstract Because of the effect of silicon on the formation of oxide scale, black strip defect is common on the surface of compact strip production (CSP) hot-rolled silicon steel, which leads to difficulty in pickling process compared with plain carbon steels. Although high-temperature oxidation of Fe-Si alloy has been discussed a lot, few studies have explained the mechanism of black strip defect generated on the surface of hot-rolled silicon steel and proposed means to prevent it effectively. Thermogravimetric analyzer (TGA) is used to simulate oxidation of Fe-2��2Si alloy for 30 min under air condition, and temperature range is from 1000 to 1150 ��. Effect of rolling deformation on scale morphology is also discussed. Electron probe microanalysis (EPMA) is used to analyze cross-sectional morphology and elemental distribution of the oxide scale. Schematic diagram of formation of black strip defect is obtained, which helps to provide theoretic basis for proposing of solutions for the problem. It is proposed that lowering furnace temperature and shortening time to stay at high temperature condition after rolling will be helpful to relieve the black strip problem.
|
|
Received: 06 June 2012
Published: 23 August 2013
|
|
Corresponding Authors:
Xiao-Jiang
E-mail: oxidescale@163.com
|
|
|
|
| [1] |
DA Chuan-li,YANG Geng-wei,MAO Xing-ping,,YU Chi-bin,HE Xian-ling,CAI Zheng,. Effect of austenite deformation on phase transformation behavior of 50CrV4 steel[J]. Chinese Journal of Iron and Steel, 2017, 29(5): 411-419. |
| [2] |
LI Sheng-cun. Discussion of the red rust on the surface of high Si high strength steel[J]. Chinese Journal of Iron and Steel, 2017, 35(5): 47-50. |
| [3] |
GUO Jing,CHENG Shu��sen,LI Ji��peng,,YAN Kun ,MEI Ya��guang. Precipitation behavior of carbon bearing inclusion in a slab for low carbon Al��killed steel[J]. Chinese Journal of Iron and Steel, 2016, 28(4): 21-27. |
| [4] |
WANG Chang,YU Yang,WANG Lin,PANG Zai- gang,CHEN Jin,JIAO Hui- li. Effects of C and P on blistering behavior of scale of hot rolled strip[J]. Chinese Journal of Iron and Steel, 2016, 28(3): 74-79. |
| [5] |
FU Song-yue��REN Yong��CHENG Xiao-ru��WANG Hao��FAN Jing-guo��SHEN Jin-long. Descaling property of third oxide scale of high carbon steel wire[J]. Chinese Journal of Iron and Steel, 2016, 51(3): 73-77. |
| [6] |
WEI Bing��HAN Bin��YANG Yi��LIU Yang��TAN Wen��WANG Shui-ze. Cause analysis of typical surface defect of hot-rolled ultra-low carbon steel[J]. Chinese Journal of Iron and Steel, 2016, 34(2): 42-46. |
|
|
|
|
2013, Vol. 20 