| Effect of Controlled Cooling on Microstructure and Mechanical Properties of H-Beam |
| GUO Fei1,ZHAO Xian-ming1,WANG Li-na1,WU Di1,WANG Guo-dong1,NING Zhong-liang2 |
1. State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110819,Liaoning, China
2. Fushun New Iron and Steel Company Ltd��, Fushun 100044, Liaoning, China |
|
|
|
|
Abstract Based on ANSYS, an analytical model was established for H-beam during controlled cooling. The temperature fields during controlled cooling and air cooling were analyzed and the microstructure and mechanical properties for different parts of H-beam were discussed in detail. After the H-beam was controlled cooled for 4��5 s, its mean surface temperature decreased from 850 to 460 ��, and the lowest and the highest temperatures were measured at edge of flange and at R corner, respectively. Whereas, for the H-beam air-cooled for 30 s, the mean temperature at R corner and web was 700 and 540 ��, respectively. The microstructures for different parts of H-beam consisted of ferrite and pearlite, and the grain size at R corner was coarser than those at flange and web. The difference of yield and tensile strengths of web, flange and R corner was within 30 MPa, and the elongation was similar. The changes of microstructure were in good agreement with that of temperature field. In addition, the results show that the uniformity of microstructure and mechanical properties can be improved by increasing water flow rate at R corner.
|
|
Received: 04 June 2012
Published: 23 August 2013
|
| Fund:Item Sponsored by National Science and Technology Support Project (2007BAE30B05) |
|
Corresponding Authors:
guo
E-mail: guofei2050@yahoo.cn
|
|
|
|
| [1] |
ZHAO Gui- heng,LIU Yong- qing,ZHANG Hong- ping. New development of giant magnetostrictive materials[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 689-696. |
| [2] |
ZHANG Shao- jun,YU Hong- yang,ZHU Dong- mei,NI Bin- bin,LIU Guo- yong,JIANG Hong. Influence of phase transition latent heat on controlled cooling technological requirements of �]160mm GCr15 bearing steel bar[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 768-774. |
| [3] |
XU Tian- han,FENG Yao- rong,WANG Dang- hui. Influence of hydrogen on mixed- mode ��/�� fracture toughness of casing- drilling steels[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 749-755. |
| [4] |
ZHU De- qing��XU Meng- jie��PAN Jian��YANG Cong- cong��TIAN Hong- yu. Experimental research to improve ballability of ultrafine concentrate[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 704-710. |
| [5] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
| [6] |
FENG Hao��JIANG Zhou-hua��LI Hua-bing��HAN Yu��LUO Yi��DING Wei. Influence of austenitizing temperature on microstructure and mechanical properties of high nitrogen bearing steel 30Cr15Mo1N[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 92-98. |
|
|
|
|
2013, Vol. 20 