| Effect of Annealing Temperature on Recrystallization Behavior of Cold Rolled Ti-Microalloyed Steel |
| HUO Xiang-dong1,MAO Xin-ping2,L�S Sheng-xia1 |
1. School of Material Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China
2. Guangzhou Zhujiang Steel Co��, Ltd��, Guangzhou 510730, Guangdong, China |
|
|
|
|
Abstract In order to develop cold rolled Ti-microalloyed steel strips, the effects of annealing temperature on recrystallization behavior of experimental steel were researched by optical microscopy (OM), transmission electron microscopy (TEM) and Vickers hardness test. The annealing treatment could be divided into three distinct stages: recovery, recrystallization and grain growth. Recrystallization took place from 933 to 1033 K, during which a large number of recrystallized grains appear and hardness drops sharply. The morphology and size of TiN particles nearly remained unchanged at different stages of processing. With increasing annealing temperature, nanometer precipitates coarsened and the dislocation density was significantly reduced. In comparison with annealing time, annealing temperature was more crucial for recrystallization of cold rolled Ti-microalloyed steel. It could be concluded that the pinning force of nanometer particles on dislocations increased the recrystallization temperature. At higher annealing temperature, recrystallization took place because of precipitates coarsening caused by Ostwald ripening.
|
|
Received: 17 February 2012
Published: 16 September 2013
|
|
Corresponding Authors:
Xiang-Dong HUO
E-mail: hxdustb@163.com
|
|
|
|
| [1] |
FAN Ming- qiang,,MAO Lei,,ZHANG Yun- fei,TIAN Zhi- qiang,SUN Zhong- hua,QIN Sen. Effects of temperature rise on deformation behavior and microstructure of H13 steel during high temperature compression process[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 756-761. |
| [2] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
| [3] |
ZHANG Shi-wei������YANG Ming������LIANG Yi-long������JIANG Yun����LONG Shao-lei����. Constitutive equations and dynamic recrystallization behaviors of 20CrNi2Mo steel at stage of high temperature deformation[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 97-105. |
| [4] |
LIU Zi- long,WANG Zhi- meng,XING Peng- da,CAO Wen- quan,PENG Yan,WANG Yu- hui. Static recrystallization behavior of GCr15 bearing steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 671-677. |
| [5] |
HUANG Xiang-bin,BAO Si-qian,ZHAO Gang,XU Yang,SONG Na-na,LIU Bing-bing. Primary recrystallization kinetics and texture evolution during annealing of low temperature grain-oriented silicon steel[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 577-582. |
| [6] |
GONG Qian-jiang��������LIANG Yi-long������ ��YANG Ming��������JIANG Yun��������XU Xiang������. Phenomenological constitutive model and dynamic recrystallization behavior of 20CrMnTiH steel[J]. Chinese Journal of Iron and Steel, 2017, 52(6): 67-75. |
|
|
|
|
2013, Vol. 20 