Microscopic Response of TRIP Steels to Prestrain During Plastic Deformation |
YU Hai-yan |
School of Automotive Engineering, Tongji University, Shanghai 201804, China |
|
|
Abstract In order to uncover the mechanism of elastic modulus degradation during plastic deformation, uniaxial tensile test of transformation-induced plasticity (TRIP) steels under different prestrain levels was carried out. The real elastic modulus unloaded at each prestrain was calculated by linearly fitting. The microstructure evolution with plastic strain and the fracture morphology were monitored by using a scanning electron microscope (SEM). Dislocation density and its distribution were detected under a transmission electron microscope (TEM). Microscopic mechanism of the elastic modulus degradation of TRIP steels was discussed in detail. Experimental results indicated that the investigated TRIP600 steel was of severe elastic modulus degradation during plastic deformation. The new-born martensite distributed among the retained austenite, resulting in the combination of good ductility and high strength for TRIP steels. It was the change of dislocation movement that induced the variation of atomic binding force and finally led to the variation of elastic modulus.
|
Received: 09 April 2012
Published: 16 September 2013
|
Fund:;Fundamental Research Funds for the Central Universitie |
Corresponding Authors:
Hai Yan
E-mail: yuhaiyan@tongji.edu.cn
|
|
|
|
[1] |
YIN Cun-hong��LIANG Yi-long. Friction induced wear and martensite deformation behavior of 20CrNi2Mo steel[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 81-86. |
[2] |
ZHANG Hai-long,GAO Yi-fei,XU Ting-dong. Computation of grain-boundary elastic modulus of steel[J]. Chinese Journal of Iron and Steel, 2017, 29(4): 329-334. |
[3] |
XU Wei-cheng��ZHANG Hua��LUO Dan-xia. Analysis of stress rate of tensile test method at room temperature in GB/T 228.1-2010[J]. Chinese Journal of Iron and Steel, 2016, 34(6): 56-58. |
[4] |
CHEN Jia��long ,YU Wan��hua,CHEN Su��dong,XIA Qiang��qiang. Transformation rule of TRIP780 steel in isothermal bainite area[J]. Chinese Journal of Iron and Steel, 2016, 28(4): 64-68. |
[5] |
LI Xia��WANG Xi-gang��LIU Hong-yi. Effect of intercritical annealing temperature on microstructure and properties of TRIP steel[J]. Chinese Journal of Iron and Steel, 2016, 51(10): 69-71. |
[6] |
MA Hong-ke�� WANG Zhi-miao. An ANSYS-based fatigue life analysis between DP steel and TRIP steel plate[J]. Chinese Journal of Iron and Steel, 2015, 33(6): 21-23. |
|
|
|
|