Texture Evolution of Columnar Grains in Electrical Steel During Hot Rolling |
SHAO Yuan-yuan1,YANG Ping1,FU Yong-jun1,2,MAO Wei-min1 |
1. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China 2. Cold Rolling Silicon Steel Division, Angang Steel Company Limited, Anshan 114021, Liaoning, China |
|
|
Abstract Columnar grains in cast slabs of electrical steel show strong anisotropy in grain orientation and morphology and thus influence the subsequent microstructure and texture after hot rolling significantly. The texture evolution of hot rolled sheets containing initial columnar grains with their <100> directions approximately parallel to the rolling direction (RD), transverse direction (TD) and normal direction (ND) of the hot rolled sheets was investigated by using EBSD technique. The results indicated that, whatever the initial texture of the columnar grains was, typical Goss, brass-type and copper-type shear texture component could develop in shear-deformed surface region. The copper-type texture formed under the maximum shearing force with the fine, sheared or dynamically recrystallized grains, and Goss grains were mainly elongated and deformed grains, while brass grains behaved between them. Additionally, the rotating relationship of the three types of shear textures was different due to the restriction of grain boundaries. In homogenously deformed center region, the RD sample contained more {112}<110> grains, and TD sample was covered by {100} textures such as {100}<011> and {100}<021> with coarse grains, while the ND sample developed many {100}<001> grains which were attributed to more {100} grains in the initial sample. Remarkable texture transition occurred on both sides of grain boundaries when {110} grains were adjacent to ��-fiber texture grains. It was found that significant texture gradient and preferred distribution of rotating axis existed in the soft orientation grains on the ��-fiber when the grains neighbored hard grains on ��-fiber.
|
Received: 21 March 2012
Published: 14 October 2013
|
|
|
|
[1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
[2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
[3] |
JIANG Zhou-hua��ZHANG Xin-fa��LIU Fu-bin��GONG Wei. Harmful impurities control of raw material used in Ni-based superalloy production[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 1-10. |
[4] |
SONG Guang-yi��YANG Quan��WANG Xiao-chen��ZHANG Xi-bang�� WANG Feng-mei��WANG Qiu-na. Work roll wear law for hot strip temper mill[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 54-59. |
[5] |
WANG Bing-xing��XIONG Lei��ZHANG Tian��WANG Zhao-dong��WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 60-65. |
[6] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
|
|
|
|