Wear Behavior and Mechanism of Spheroidal Graphite Cast Iron |
YANG Zi-run1,LI Dong-sheng2,WANG Lan2,WANG Shu-qi2,WEI Min-xian2 |
1. School of Materials Engineering, Yancheng Institute of Technology, Yancheng 224051, Jiangsu, China 2. School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China |
|
|
Abstract Wear behavior and mechanism of spheroidal graphite cast iron were studied on a pin-on-disk elevated temperature wear tester. The phase and morphology of worn surfaces were examined by X-ray diffraction and scanning electron microscopy. Results show that with an increase of load, wear rate of spheroidal graphite cast iron gradually increases under low loads, rapidly increases or potentially increases under high loads; wear rate increases with increasing ambient temperature. At 25-200 ��, adhesive wear prevails; oxidative wear and adhesive wear coexist at 400 ��. As load surpasses 150 N at 400 ��, extrusive wear appears. The elevated-temperature wear of spheroidal graphite cast iron is a physical and chemical process including the following reactions: xFe+y/2O2��FexOy, 2C+O2��2CO and FexOy+yCO��xFe+yCO2. Hence, at 400 ��, the amount of graphite and tribo-oxides are substantially reduced because of reductive function of graphite. It can be suggested that wear-reduced effect of graphite and tribo-oxides is impaired.
|
Received: 11 April 2012
Published: 14 October 2013
|
Corresponding Authors:
wang
E-mail: shuqi_wang@ujs.edu.cn
|
|
|
|
[1] |
XU Tian- han,FENG Yao- rong,WANG Dang- hui. Influence of hydrogen on mixed- mode ��/�� fracture toughness of casing- drilling steels[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 749-755. |
[2] |
HUANG Rui,WANG Huan- rong,LIU Jun- liang. Influence of coiling temperature on nano- precipitated particles of advanced nano- precipitate strengthened high strength steel[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 684-689. |
[3] |
YANG Ting,SU Hang,LUO Xiao-bing,CHAI Feng,ZHANG Zheng-yan. Cross section microstructure and homogeneity of mechanical properties of as quenched high strength ship steel[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 583-589. |
[4] |
LEI Dong��REN Yong��CHENG Xiao-ru��LAN Kun��QIU Jun��HUANG Da-jun. Effect of heat treatment on microstructure and mechanical properties of 316L/Q235 stainless steel composite panel[J]. Chinese Journal of Iron and Steel, 2017, 52(5): 66-71. |
[5] |
LI Meng��SONG Xiao-jie. Reason analysis and improvement on the non-yield point of HRB400 wire rod[J]. Chinese Journal of Iron and Steel, 2017, 35(3): 7-9. |
[6] |
WANG Yu-nan. Effects of[w(Mn)]on thermal properties of Fe-Mn-C steels[J]. Chinese Journal of Iron and Steel, 2017, 52(10): 51-58. |
|
|
|
|