| Effect of Finishing Rolling Temperature on Microstructure and Mechanical Properties of Microalloyed TRIP Steels |
| MI Zhen-li,JIANG Hai-tao,LI Zhi-chao,CHEN Mei-fang,WANG Zhi-gang |
| National Engineering Research Center for Advanced Rolling Technology, University of Science and Technology Beijing, Beijing 100083, China |
|
|
|
|
Abstract Different samples of TRIP (transformation induced plasticity) steel obtained by two different hot-rolling schedules are investigated by using a SEM (scanning electron microscope). The microstructure is characterized by using an OM (optical microscope) for phase distribution and by EBSD (electron backscatter diffraction) for texture and phase mapping. ODF (orientation distribution function) graphs are used to investigate the effect of recrystallization behavior of the hot-deformed austenite on phase transformation during the controlled cooling process. The mechanical behavior is interpreted in terms of the strength of both hard and soft phases, in combination with the quantity, location and transformation kinetics of the mechanically induced martensite (TRIP effect). The results show that more austenite grains exist in the steels obtained at finishing rolling temperature (FRT) of 750 ��, which inherited the deformation structure after the hot-rolling process. The instantaneous n value (ni) of those steels is kept high during a large range of strain before failure, while the tensile strength and total elongation of the steels with respect to the different finishing rolling temperatures do not show any significant differences.
|
|
Received: 17 May 2012
Published: 14 October 2013
|
|
|
|
| [1] |
YIN Cun-hong��LIANG Yi-long. Friction induced wear and martensite deformation behavior of 20CrNi2Mo steel[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 81-86. |
| [2] |
Yong Li,Lei Fang. Robust multi-objective optimization of rolling schedule for tandem cold rolling based on evolutionary direction differential evolution algorithm[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 795-802. |
| [3] |
Dong-dong Zhuang,*,Lei-gang Wang,Yao Huang,Xiao-min Li,Hua-yang Zhang,De-wei Ren. Microstructure and texture evolution during recrystallization of low-carbon steel sheets[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 84-90. |
| [4] |
Si-qian Bao,,*,Yang Xu,Gang Zhao,,Xiang-bin Huang,Huan Xiao,Chuan-long Ye, Na-na Song,Qing-ming Chang. Microstructure, texture and precipitates of grain-oriented silicon steel produced by thin slab casting and rolling process[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 91-96. |
| [5] |
Jian KANG,Cheng-ning LI,Xiao-lei LI,,Jin-hua ZHAO,Guo YUAN,Guo-dong WANG. Effects of Processing Variables on Microstructure and Yield Ratio of High Strength Constructional Steels[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 815-821. |
| [6] |
Gan- lin XIE,An HE,Hai- long ZHANG,Gen- qi WANG,Xi- tao WANG. A Physically Based Dynamic Recrystallization Model Considering Orientation Effects for a Nitrogen Alloyed Ultralow Carbon Stainless Steel during Hot Forging[J]. Chinese Journal of Iron and Steel, 2016, 23(4): 364-371. |
|
|
|
|
2013, Vol. 20 