In-Situ Observation of Proeutectoid Ferrite Growth Process in Carbon Steel Under Continuous Cooling Conditions |
JIN Guang-can,CHEN Shu-ying,LI Qing-chun,CHANG Guo-wei,YUE Xu-dong |
School of Materials Science and Technology, Liaoning University of Technology, Jinzhou 121001, Liaoning, China |
|
|
Abstract The growth of proeutectoid ferrite in Fe-0��15%C-0��8%Mn carbon steel during continuous cooling process was observed in-situ and tracked dynamically by using a high-temperature confocal scanning laser microscope (HTCSLM), and the growing process was also investigated. The growth regularity of proeutectoid ferrite plates within austenite was obtained by analyzing the growth fashions and directions and quantitatively studying the growth rates. The results show that the proeutectoid ferrite plates grow in the fashion of creeping, twisting, branching off and deflection within austenite grain. The proeutectoid ferrite plates can grow up along preferential orientation but not strictly. Its growth direction fluctuates and changes in a small range. The growth rate also changes with the change in growth fashion and direction. When the proeutectoid ferrite grows in the fashion of deflection, the average growth rate of proeutectoid ferrite before its deflection is about 61��9, and 46��2 ��m/s after the 15�� deflection. At the beginning of proeutectoid ferrite growing, there is a fast growing stage. As the tip of proeutectoid ferrite extends forward continuously, the growth rate will slow down. Therefore, it will induce the proeutectoid ferrite to deflect and grow along another favorable direction, then it will grow rapidly again.
|
Received: 04 June 2012
Published: 14 October 2013
|
Fund:Scientific Director Fund of National Natural Science Foundation of China |
|
|
|
[1] |
DU Chen-wei��LAN Peng��LI Yang��LU Jue-yu��ZHANG Jia-quan��JIANG Zhong-kuai��SU Rui-xian��ZHOU Xiu-li��WANG Hong-feng. Thermodynamic analysis on solidification and solid phase transformation control of J55 steel continuous casting slab[J]. Chinese Journal of Iron and Steel, 2017, 42(1): 64-67. |
[2] |
L�� Chang-bao. Analysis on pseudo-eutectoid pearlite in the low carbon steel[J]. Chinese Journal of Iron and Steel, 2015, 50(3): 68-72. |
[3] |
CHEN Ran,,CHEN Zhao- ping,XU Ying- tie,ZHOU Can- dong,SHU Da. In- situ observation of behaviors of inclusions in bearing steel[J]. Chinese Journal of Iron and Steel, 2015, 27(12): 48-53. |
[4] |
WANG Li-min,PENG Meng-du,,LIU Zheng-dong,YANG Gang,LEI Jiu-fang. Microstructure Transformation Law of Medium Carbon Cr-Mo-V Steel During Continuous Cooling Process[J]. Chinese Journal of Iron and Steel, 2014, 26(12): 70-74. |
[5] |
QI Jiang-hua,YANG Cheng-wei,ZHU Wang-jun,OU Tie,LIU Yang,JI Yu. Effect of Heat and Insulation Treatment on MnS Inclusion in Heavy Rail Steel[J]. Chinese Journal of Iron and Steel, 2013, 48(11): 79-83. |
[6] |
ZHANG Zheng-yan1,2,YONG Qi-long2,SUN Xin-jun2,QI Hai-quan3,SHI Jin2. Effect of Nb on Pearlite Transformation Behavior of Eutectoid Steel[J]. Chinese Journal of Iron and Steel, 2012, 47(4): 79-83. |
|
|
|
|