| Numerical Simulation and Experimental Study on Interlock Deformation for Roll Formed U-Section Steel Piling |
| FENG Guang-hong1,ZHANG Pei1,ZHANG Hong-liang1,ZHOU Xu-chang2,ZHAO Yong2 |
1. Metallurgical Technology Institute, Central Iron and Steel Research Institute, Beijing 100081, China
2. Taian Kenuo Profile Steel Co. , Ltd. , Taian 271038, Shandong, China |
|
|
|
|
Abstract The interlock of a roll formed U-section sheet steel piling under loading was analyzed by means of numerical simulation, and meanwhile the tensile failure experiment was conducted. The results indicated that under the same load, the interlock corners of roll formed steel piling are not only the regions with the lowest safety factor, but also the regions with the highest stress; there are two slippages in the tensile instability process of interlock. Each slippage can be regarded as a failure, and different types of failure mode should be used to evaluate the performance of steel pilings according to different applications. Due to the work hardening effect during the roll forming process, the hardness of the interlock material increases by 16% compared with that of the original sheet steel. It was also found that the instability strength obtained in tensile failure test is only 15. 6% of the tensile strength of the original sheet steel.
|
|
Received: 16 July 2012
Published: 18 November 2013
|
|
Corresponding Authors:
Guang-Hong Feng
E-mail: fgh@vip.sina.com
|
|
|
|
| [1] |
ZHANG Shao- jun,YU Hong- yang,ZHU Dong- mei,NI Bin- bin,LIU Guo- yong,JIANG Hong. Influence of phase transition latent heat on controlled cooling technological requirements of �]160mm GCr15 bearing steel bar[J]. Chinese Journal of Iron and Steel, 2017, 29(9): 768-774. |
| [2] |
WANG San- zhong ,HUANG Zhao- meng,YU Hui,,DU Feng- shan,. Influence of parameters on molten pool field during twin- roll casting process[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 643-648. |
| [3] |
CHEN Li-feng. Numerical simulation and process analysis of Al2O3 inclusion removal in RH refining process[J]. Chinese Journal of Iron and Steel, 2017, 52(7): 42-46. |
| [4] |
YUAN Hui,JIN Yan,XUE Zheng-liang,WANG Wei,LUO Xiao,CHENG Chang-gui. Effect of unsteady flow of molten iron in blast furnace on hearth bottom erosion[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 544-550. |
| [5] |
YANG Wen-kai,YIN Yuan-de,LI Sheng-zhi. Analysis of continuous seamless steel tube rolling with two-roll grooves using backing mandrel[J]. Chinese Journal of Iron and Steel, 2017, 29(6): 481-487. |
| [6] |
MA Fu-tao��ZHANG Jian-liang��LIU Yun-cai. BF burden distribution numerical simulation based on genetic algorithm[J]. Chinese Journal of Iron and Steel, 2017, 52(6): 18-25. |
|
|
|
|
2013, Vol. 20 