| Optimization Evaluation Test of Strength and Toughness Parameters for Hot-Stamped High Strength Steels |
| YING Liang,LU Jin-dong,CHANG Ying,TANG Xing-hui,HU Ping,ZHAO Kun-min |
| School of Automotive Engineering, State Key Laboratory of Structural Analysis for Industrial Equipment,Dalian University of Technology, Dalian 116024, Liaoning, China |
|
|
|
|
Abstract Use of hot-stamped high strength steels (HSHSS) not only reduces the vehicle weight, but also improves the crash safety, therefore more and more mentioned steels are used to produce automobile parts. However, there are several problems especially the low ductility and toughness, which have restricted the application of HSHSS in automobile body. Suitable process parameters are very crucial to improve strength and toughness. In order to study the effect of austenization temperature, soaking time and start deformation temperature on strength and toughness of boron steel 22MnB5, an L9 (34) orthogonal experiment which was analyzed by means of comprehensive evaluation was carried out based on Kahn tear method to obtain the value of fracture toughness. The results indicate that the excellent formability, high strength and toughness of boron steel 22MnB5 with 1. 6 mm in thickness are obtained when the austenization temperature is in the range of 920-950 ��, the soaking time is 1 min and the start deformation temperature is in the range of 650-700 ��. The optimal parameters were used for typical hot stamping structural parts tests. Properties of samples such as tear strength, unit initiation energy and ratio of strength to toughness (RST) were improved by 10. 91%, 20. 32% and 22. 17%, respectively. Toughness was increased substantially on the basis of a small decrease of strength.
|
|
Received: 20 June 2012
Published: 18 November 2013
|
|
|
|
| [1] |
Ming-bo Zhou,Jing-lin Tang,*,Jie Yang,Cun-yu Wang. Tailored properties of a novelly-designed press-hardened 22MnMoB steel[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 508-512. |
| [2] |
Qing Shao*,Tao Xu,Tatsuo Yoshino,Nan Song. Multi-objective optimization of gas metal arc welding parameters and sequences for low-carbon steel (Q345D) T-joints[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 544-555. |
| [3] |
Hui-hui Xiong,,*,Heng-hua Zhang,Hui-ning Zhang,Yang Zhou. Effects of alloying elements X (X=Zr, V, Cr, Mn, Mo, W, Nb, Y) on ferrite/TiC heterogeneous nucleation interface: first-principles study[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 328-334. |
| [4] |
Meng-xuan Guo,Kai-xiang Gao,Wu-rong Wang,Xi-cheng Wei. Microstructural evolution of Al-Si coating and its influence on high tempera-ture tribological behavior of ultra-high strength steel against H13 steel[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 1048-1058. |
| [5] |
Ji-chun Yang,Xiang-jun Liu,Gui-xiao Jia*,Xiao-yang Fu. A first-principles study on electronic structures and elastic properties of metal doped ��-Fe(N) high nitrogen steel[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 103-110. |
| [6] |
Mahmudun Nabi CHOWDHURY,Ju��ri KIM,Sung��tae HONG,Jin��wook JUNG,Heung��nam HAN,Sang��woo SO. Tailoring of Mechanical Properties of Indirect Hot Stamping Steel Tubes by Laser Assisted Local Rapid Heating[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 949-954. |
|
|
|
|
2013, Vol. 20 