| Elasto-Plastic Test of Q235 Steel Bending Beam With Cracking Resistance |
| WANG Li-min1,FENG Ying1,CHEN Fan-xiu1,WANG Hai-ying2,WANG Dong-xu1 |
1. Science School, Qingdao Technological University, Qingdao 266033, Shandong, China
2. Institute of Mechanics, Chinese Academy of Sciences, Beijing 100190, China |
|
|
|
|
Abstract More than 30 bending beams with rectangular cross-section and different thicknesses and heights were prepared from Q235 steel. The specimen dimensions were about 240 mm (length)��60 mm (height)��70 mm (thickness). Flaws were cut along its middle line with a wire cutter, with lengths ranging from 6 to 35 mm. Each specimen was tested with three-point bend loading, and a process curve was obtained between load and the displacement of the loading point, in order to analyze the fracture process when opening the crack. A deformation near the prefabricated crack was observed in the testing period, and the variation of the fracture characteristic parameters was analyzed for different sizes. For a comprehensive understanding of carbon steel fracture resistance behavior, its elasticity and plasticity were established by determining its Young��s modulus and Poisson��s ratio with an optical strain gauge. This gauge was also used for the loading process test. It was found that the fracture toughness varied with the dimensions, and the toughness of the elastic limit loading was almost constant. Using the relationship of crack resistance stress intensity factor and fracture criterion, the bearing capacity of the material structure could be estimated, which shows a good agreement with the experimental test data.
|
|
Received: 15 November 2011
Published: 18 November 2013
|
|
Corresponding Authors:
Limin WANG
E-mail: wanglimin@qtech.edu.cn
|
|
|
|
| [1] |
WANG Li,,LI Guang- qiang,,,LIU Yu,,ZHANG Zhao,,LI Ya- wei��XU Xiao- feng. Interaction between ultra- low carbon liquid steel and MgO- C refractories containing different carbon contents[J]. Chinese Journal of Iron and Steel, 2017, 29(8): 616-625. |
| [2] |
LUO Yan-zhao��JI Chen-xi��DENG Xiao-xuan��PAN Hong-wei��ZENG Zhi��CUI Yang. Optimization of mold flux to improve surface quality of ultra-low carbon IF steel[J]. Chinese Journal of Iron and Steel, 2017, 52(4): 38-43. |
| [3] |
ZHOU Feng-luan. Error analysis of[KIC]calculated by[J]integral[J]. Chinese Journal of Iron and Steel, 2017, 35(4): 52-53. |
| [4] |
LIU Dong��XUE Huan��WU Li-xin��DU Li-ying. CTOD evaluation of bridge steel Q420qD by failure assessment diagram method[J]. Chinese Journal of Iron and Steel, 2016, 34(6): 28-33. |
| [5] |
LUO Yan-zhao��LIU Bai-song��YUAN Peng��GAO Pan��NI You-jin��PEI Xing-wei. Impact analysis of casting parameters on surface sliver defects for ultra-low carbon steel[J]. Chinese Journal of Iron and Steel, 2016, 41(5): 62-66. |
| [6] |
ZHANG Xu-bin��ZHANG Li-feng��YANG Wen��WANG Qiang-qiang. Basic research on oscillation marks and solidification hooks of continuous casting slabs[J]. Chinese Journal of Iron and Steel, 2016, 41(5): 58-61. |
|
|
|
|
2013, Vol. 20 