Oxidation and Thermal Fatigue Behaviors of Two Type Hot Work Steels During Thermal Cycling |
MIN Yong-an1,2,Bergstr��m Jens2,WU Xiao-chun1,XU Luo-ping1 |
1. School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China 2. Department of Materials Engineering, Karlstad University, Karlstad 65188, Sweden |
|
|
Abstract Thermal fatigue test has been carried out on widely used hot work steel 4Cr5MoSiV1 and a low alloyed steel 3Cr3MoV in temperature range of 200 to 700 ��. Tempering resistance, as well as high temperature hardness/strength of steel specimens, works as a dominating material parameter on thermal fatigue resistance. During the heating period, high hardness can depress the inelastic deformation. This deformation is the origination of tensile stress, which acts as the driving force of heat checking during the cooling period. The cyclic strain-oxidation interaction can speed up the damage on surface defects, which plays an obvious role in initiation of thermal cracks. On 4Cr5MoSiV1 steel specimens, borders between the matrix and inclusions such as titanium compounds, or lager carbides such as primary carbides, are focused by strain and attacked by oxidation, and are main initiating places of cracks. While on 3Cr3MoV steel specimens, larger strain causes plastic deformation concentrating around grain boundaries. Then the following oxidation accelerates this grain boundary damage and creates cracks.
|
Received: 06 September 2012
Published: 18 November 2013
|
Corresponding Authors:
Yong-an yongMIN
E-mail: mya@staff.shu.edu.cn
|
|
|
|
[1] |
Yu-cheng Lei,,*,Xiao-kai Guo,Hong-xia Chang,Tian-qing Li,,Qiang Zhu,Gang Chen, Long-ren Xiao. Cavitation erosion behavior of CLAM steel weld joint in liquid lead-bismuth eutectic alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 935-942. |
[2] |
Ying-yi Zhang,Wei Lv,Xue-wei Lv,Chen-guang Bai,Ke-xi Han,Bing Song. Oxidation kinetics of ilmenite concentrate by non-isothermal thermogravimetric analysis[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 678-684. |
[3] |
Rui Wang,Yan-ping Bao,*,Yi-hong Li,Tai-quan Li,Di Chen. Effect of slag composition on steel cleanliness in interstitial-free steel[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 579-585. |
[4] |
Hong-huan Mao,Xing Qi,Jing Cao,Li-cong An,Yi-tao Yang*. Effect of Si on high temperature oxidation of 30Cr13 stainless steel[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 561-566. |
[5] |
Yong-jiang Huang,,,*,Peng Xue,Xiang Cheng,Ya-ming Wang,Fu-yang Cao,**, Zhi-liang Ning, Jian-fei Sun,. Plasticity improvement of a Zr-based bulk metallic glass by micro-arc oxidation[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 416-420. |
[6] |
Shi-lu Zhao,*,Zhen Zhang,Jun Zhang,Jian-ming Wang,Zheng-gui Zhang,Shuang-hong Wang. High temperature oxidation resistance of CrN/(Ti,Al,Zr,Cr)N bilayer films deposited by multi-arc ion plating[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 343-349. |
|
|
|
|