| Influence of Cast Dimension on Rotary Bending High Cycle Fatigue Properties of Single Crystal Superalloy |
| SHI Zhen-xue,HAN Mei,LIU Shi-zhong,LI Jia-rong |
| Science and Technology on Advanced High Temperature Structural Materials Laboratory, Beijing Institute of Aeronautical Materials, Beijing 100095, China |
|
|
|
|
Abstract Samples of DD3 single crystal superalloy with different dimensions were cast in the directionally solidified furnace with high temperature gradient. The effect of cast dimension on the rotary bending high cycle fatigue (HCF) properties of the alloy was investigated at 800 �� in ambient atmosphere. SEM was used to examine the fracture surface and fracture mechanism of the alloy. The results show that the rotary bending HCF properties of the alloy decreases with increasing cast dimension. The cast dimension has little effect on the HCF fracture mechanism of the alloy. The HCF fracture mechanism of the alloy with different cast dimensions is all quasi-cleavage fracture. The fatigue cracks initiated on the surface or near the surface of the specimens. The crack would propagate along {111} octahedral slip planes. Typical fatigue arc and striation formed on fatigue crack steady propagation. The degeneration of HCF properties is due to the increase of dendrite arm spacing and size of �á� phase particles and maximal microporosity.
|
|
Received: 09 October 2012
Published: 17 December 2013
|
|
Corresponding Authors:
Shi Zhenxue
E-mail: shizhenxue@126.com
|
|
|
|
| [1] |
Zhen-xue Shi,Shi-zhong Liu,Xiao-dai Yue,Li-jie Hu,Wan-peng Yang,Xiao-guang Wang,Jia-rong Li. Effect of cellular recrystallization on tensile properties of a nickel-based single crystal superalloy containing Re and Ru[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 1059-1064. |
| [2] |
Zhen-xue SHI,Shi-zhong LIU,Jian YU,Jia-rong LI. Tensile Behavior of the Second Generation Single Crystal Superalloy DD6[J]. Chinese Journal of Iron and Steel, 2015, 22(8): 738-742. |
| [3] |
SHI Zhen-xue,LI Jia-rong,LIU Shi-zhong,WANG Xiao-guang,YUE Xiao-dai. Effects of Ru on Solidification Characteristic and Microstructures of Ni-Based Single Crystal Superalloy[J]. Chinese Journal of Iron and Steel, 2013, 20(3): 74-78. |
| [4] |
SHI Zhen-xue,LI Jia-rong,LIU Shi-zhong. Effect of Hf on Stress Rupture Properties of DD6 Single Crystal Superalloy After Long Term Aging[J]. Chinese Journal of Iron and Steel, 2012, 19(7): 66-70. |
| [5] |
SHI Zhen-xue,LI Jia-rong,LIU Shi-zhong,ZHAO Jin-qian. Effects of Dendritic Orientation on Stress Rupture Properties of DD6 Single Crystal Superalloy[J]. Chinese Journal of Iron and Steel, 2011, 18(10): 66-71. |
| [6] |
ZHANG Bing;TAO Chun-hu;LU Xin;LIU Chang-kui;HU Chun-yan;BAI Ming-yuan. Recrystallization of a Single Crystal Nickel-Base Superalloy[J]. Chinese Journal of Iron and Steel, 2009, 16(6): 75-79. |
|
|
|
|
2013, Vol. 20 