| Improvement of Grain Size and Dome Height of Microalloyed Steels Using Taguchi Method Based on Grey Relational Grade in Controlled Rolling |
| Mohsen Ayaz1,Daavood Mirahmadi Khaki2,Nasrollah Bani Mostafa Arab1 |
1. Department of Mechanical Engineering, Shahid Rajaee Teacher Training University, Tehran 1678815811, Iran
2. Department of Materials Engineering, Shahid Rajaee Teacher Training University, Tehran 1678815811, Iran |
|
|
|
|
Abstract An efficient approach was introduced for improving the condition of major controlled rolling process parameters of roughing, finishing and coiling temperatures and optimizing these parameters to obtain minimum grain size and maximum dome height simultaneously. Taguchi method combined with grey relational analysis was applied to achieve optimum grain size and dome height during controlled rolling process. For this purpose, four levels for the above temperatures were chosen and sixteen experiments were conducted based on orthogonal array of Taguchi method. Based on Taguchi approach, signal-to-noise (S/N) ratios were calculated and used in order to obtain the optimum levels for every input parameter. Analysis of variance revealed that finishing and coiling temperatures have the maximum effect on the grain size and dome height of microalloyed steels. The confirmation tests with the optimal levels of parameters indicated that the grain size and dome height of controlled rolled microalloyed steels can be improved effectively through this approach.
|
|
Received: 08 July 2013
Published: 17 December 2013
|
|
Corresponding Authors:
Mohsen Ayaz
E-mail: mohsen.ayaz@yahoo.com
|
|
|
|
| [1] |
Hai-feng Xu,,*,Feng Yu,Chang Wang,Wan-li Zhang,Jian Li,Wen-quan Cao. Comparison of microstructure and property of high chromium bearing steel with and without nitrogen addition[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 206-213. |
| [2] |
Wei YU,Bao��sheng XIE,Ban WANG,Qing��wu CAI,Shi��xin XU. Effect of Rolling Process on Microstructure and Properties of 95CrMo Drill Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 910-916. |
| [3] |
Tao SUN,,Feng YUE,,Hua- jie WU,,Chun GUO,,Ying LI,Zhong- cun MA. Solidification Structure of Continuous Casting Large Round Billets under Mold Electromagnetic Stirring[J]. Chinese Journal of Iron and Steel, 2016, 23(4): 329-337. |
| [4] |
Hui-bin WU,Di WANG,Peng-cheng ZHANG,Jin-ming LIANG,Sheng LIU,Di TANG. Influences of Alloying Elements on Oxidation Behavior of Steels and Microstructure of Oxide Scales[J]. Chinese Journal of Iron and Steel, 2016, 23(3): 231-237. |
| [5] |
Jiao LUO,Ying-gang LIU,Miao-quan LI. Three-dimensional Numerical Simulation and Experimental Analysis of Austenite Grain Growth Behavior in Hot Forging Processes of 300M Steel Large Components[J]. Chinese Journal of Iron and Steel, 2016, 23(10): 1012-1019. |
| [6] |
Qi SUN,,Jian WANG,,Hua-bing LI,Yue LI,,Ya-di HU,,Jin-gang BAI,Pei-de HAN,. Chi Phase after Short-term Aging and Corrosion Behavior in 2205 Duplex Stainless Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(10): 1071-1079. |
|
|
|
|
2013, Vol. 20 