Microstructures and Mechanical Properties of X100 Pipeline Steel Strip |
Lin-na DUAN1,2,Yu CHEN3,Qing-you LIU2,Shu-jun JIA2,Cheng-chang JIA1 |
1. School of Material Science and Engineering, University of Science and Technology Beijing, Beijing 100083,China 2. Institute for Engineering Steel, Central Iron and Steel Research Institute, Beijing 100081, China 3. China Petroleum Engineering and Construction Corporation, Beijing 100120, China |
|
|
Abstract Dynamic CCT (continuous cooling transformation) curves and effects of microstructures and M/A islands of X100 hot rolled strip on mechanical properties were studied by means of a thermal simulator, a scanning electron microscope (SEM), a transmission electron microscope (TEM), a digital micro-hardness tester and Image-Pro Plus analysis software. The results show that high contents of C and Mo can make transformation lines of acicular ferrite and bainite shift rightward. High Mo tested strip has higher strength and micro-hardness and lower toughness than the other one because lath bainite appears instead of quasi-polygonal ferrite. Tested strip with granular bainite, lath bainite and M/A islands has better mechanical properties and in the microstructures lath bainite content is around 36��5% and M/A islands are fine and disperse in the matrix.
|
Received: 11 April 2013
Published: 20 February 2014
|
|
|
|
[1] |
Yun LEI,Bing XIE,Wen- hui MA. Analysis of Crystallization Behavior of Mold Fluxes Containing TiO2 Using Single Hot Thermocouple Technique[J]. Chinese Journal of Iron and Steel, 2016, 23(4): 322-328. |
[2] |
Zheng-yan ZHANG,,Qi-long YONG,Xin-jun SUN,Zhao-dong LI,Jun-yu KANG,Guo-dong WANG. Microstructure and Mechanical Properties of Precipitation Strengthened Fire Resistant Steel Containing High Nb and Low Mo[J]. Chinese Journal of Iron and Steel, 2015, 22(4): 337-343. |
[3] |
WANG Xiao-nan,DI Hong-shuang,ZHANG Chi,DU Lin-xiu,DONG Xue-xin. Weldability of 780 MPa Super-High Strength Heavy-Duty Truck Crossbeam Steel[J]. Chinese Journal of Iron and Steel, 2012, 19(6): 64-69. |
[4] |
ZHENG Xiao-fei,KANG Yong-lin,MENG De-liang,AN Shou-yong,XIA Dian-xiu. Effect of Cooling Start Temperature on Microstructure and Mechanical Properties of X80 High Deformability Pipeline Steel[J]. Chinese Journal of Iron and Steel, 2011, 18(10): 42-46. |
[5] |
XU Feng-yun;WANG Yong-wei. CCT Curves of low carbon Mn-Si steels and development of water cooled bainitic steels[J]. Chinese Journal of Iron and Steel, 2010, 17(3): 46-50. |
[6] |
ZHANG Ji��ming;SUN Wei��hua;SUN Hao. Mechanical Properties and Microstructure of X120 Grade High Strength Pipeline Steel[J]. Chinese Journal of Iron and Steel, 2010, 17(10): 63-67. |
|
|
|
|