Mechanical Properties of Steels Treated by Q-P-T Process Incorporating Carbide-free-bainite/martensite Multiphase Microstructure |
Zhun-li TAN1,Kai-kai WANG1,Gu-hui GAO1,Xiao-lu GUI1,Bing-zhe BAI1,2,Yu-qing WENG3 |
1. Materials Science and Engineering Center, Beijing Jiaotong University, Beijing 100044, China 2. Key Laboratory of Advanced Materials, School of Materials Science and Engineering, TsinghuaUniversity, Beijing 100084, China 3. The Chinese Society for Metals, Beijing 100044, China |
|
|
Abstract Quenching-partitioning-tempering (Q-P-T) process were applied to a quenched carbide-free bainite/martensite (CFB/M) multiphase steel 40Mn2Si2Cr and its effect on the mechanical properties was studied. The results showed that the partitioning time of Q-P-T treatment can be increased greatly to 90 min or even longer. The tensile strength, elongation and product of strength and elongation (PSE) of the experimental steel can achieve 1650 MPa, about 20% and over 33 GPa��%, respectively. The significant increase of partitioning time and excellent mechanical properties could be related to the CFB microstructure introduced in the quenching process during the Q-P-T treatment.
|
Received: 19 June 2013
Published: 20 February 2014
|
Fund:National Outstanding Youth Science Foundation of China;Project guided by science and technology in Inner Mongolia Autonomous Region |
Corresponding Authors:
Zhun-Li TAN
E-mail: tzli@bjtu.edu.cn;02lzhtan@163.com
|
|
|
|
[1] |
Jian KANG,Cheng-ning LI,Xiao-lei LI,,Jin-hua ZHAO,Guo YUAN,Guo-dong WANG. Effects of Processing Variables on Microstructure and Yield Ratio of High Strength Constructional Steels[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 815-821. |
[2] |
Ming MA,Hua DING,Zheng-you TANG,Jing-wei ZHAO,Zhou-hua JIANG,Guang-wei FAN. Effects of Temperature and Strain Rate on Flow Behavior and Microstructural Evolution of Super Duplex Stainless Steel under Hot Deformation[J]. Chinese Journal of Iron and Steel, 2016, 23(3): 244-252. |
[3] |
MI Zhen-li,JIANG Hai-tao,LI Zhi-chao,CHEN Mei-fang,WANG Zhi-gang. Effect of Finishing Rolling Temperature on Microstructure and Mechanical Properties of Microalloyed TRIP Steels[J]. Chinese Journal of Iron and Steel, 2013, 20(10): 75-80. |
[4] |
ZHAO Jin-long,XI Yan,SHI Wen,LI Lin. Microstructure and Mechanical Properties of High Manganese TRIP Steel[J]. Chinese Journal of Iron and Steel, 2012, 19(4): 57-62. |
[5] |
DING Hao;DING Hua;QIU Chun��lin;TANG Zheng��you;ZENG Jian��min;YANG Ping. Formability of TRIP/TWIP Steel Containing Manganese of 18.8%[J]. Chinese Journal of Iron and Steel, 2011, 18(1): 36-40. |
[6] |
Zou De-ning;HAN Ying;ZHANG Wei;et al. [J]. Chinese Journal of Iron and Steel, 2010, 17(8): 50-54. |
|
|
|
|