| Mechanism of Effect of Microwave Modification on Pulverized Coal Combustion Properties |
| Qing-hai PANG1,Jian-liang ZHANG1,Rui MAO1,Zhe JIANG1,Tong LIU2 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing, Beijing 100083, China
2. Fushun Special Steel Shares Co. , Ltd. , Fushun 116031, Liaoning, China |
|
|
|
|
Abstract The mechanism of microwave modification on facilitating the combustion properties of pulverized coal (PC) was investigated. Experimental researches on granularity and functional group as well as combustion properties of PC before and after modification were carried out. Micromorphology observation indicated that the size of PC particles was relatively small, which was in accordance with the results of granularity analysis of PC. FT-IR (Fourier-transform infrared) spectra of two PCs indicated that the proportion of the functional groups with high activity increased after microwave irradiation. Furthermore, no valid effect of microwave was found on carbon matrix except small variations in PC particle size, which only led to subtle improvement in combustion of residual coke. Activation energies of Yungang and Yangquan PCs in temperature zone between 450-650 �� were reduced by 12. 00% and 10. 13%, respectively, which meant that microwave modification might effectively facilitate the combustion properties of PC. Nevertheless, decrease in activation energies of residual cokes was 3. 56% and 3. 67% respectively, which was subtle and can be regarded as the result of smaller particle size produced by microwave irradiation.
|
|
Received: 01 November 2012
Published: 19 March 2014
|
|
|
|
| [1] |
CHEN Shu-jun,,L�� Qing, ,BAI Rui-guo,LI Yan-jiang. High-temperature plasma pyrolysis of pulverized coal for blast furance injection at Chengsteel[J]. Chinese Journal of Iron and Steel, 2017, 29(4): 261-265. |
| [2] |
YANG Shuang��ping��GUO Shuan��quan��ZHANG Pan��hui��ZHOU Jiang��feng��WANG Miao. Influence of semi��coke on blending coal injection characteristics for blast furnace[J]. Chinese Journal of Iron and Steel, 2017, 29(3): 201-207. |
| [3] |
WANG Yi-ci,LI Hai-yang,LUO Guo-ping,LI Shuang-wei. Macrokinetics of gasification dephosphorization of converter slag by microwave carbon thermal reduction[J]. Chinese Journal of Iron and Steel, 2017, 29(2): 93-97. |
| [4] |
WANG Hai-yang,ZHANG Jian-liang,WANG Guang-wei,LIU Si-yuan,LIN Hao,XU Run-sheng. Feasibility research of brown coal injection for blast furnace[J]. Chinese Journal of Iron and Steel, 2017, 29(1): 39-43. |
| [5] |
ZHANG Jun��DAI Xiao-tian��YAN Ding-liu. New smelting-separation process based on hot air-coal combustion dealing with metallurgical solid wastes[J]. Chinese Journal of Iron and Steel, 2016, 51(8): 76-80. |
| [6] |
LI Yan-jiang,L�Y Qing,BAI Rui-guo,LIU Ran,LI Hong-wei. Combustion-supporting mechanisms of CeO2 for blast furnace pulverized coal injection[J]. Chinese Journal of Iron and Steel, 2016, 28(7): 8-12. |
|
|
|
|
2014, Vol. 21 