Morphology of Oxide Scale and Oxidation Kinetics of Low Carbon Steel |
Guang-ming CAO,Xiao-jiang LIU,Bin SUN,Zhen-yu LIU |
State Key Laboratory of Rolling and Automation, Northeastern University, Shenyang 110004, Liaoning, China |
|
|
Abstract The oxidation kinetics and composition of oxide scales on low carbon steel (SPHC) were studied during isothermal oxidation. Thermogravimetric analyzer (TGA) was used to simulate isothermal oxidation process of SPHC for 240 min under air condition, and the temperature range was from 500 to 900 ��. Scanning electron microscope (SEM) was used to observe cross-sectional scale morphology and analyze composition distribution of oxide scales. The morphology of oxide scale was classical three-layer structure. Fe2O3 developed as whiskers at the outermost layer, and interlayer was perforated-plate Fe3O4 while innermost layer was pyramidal FeO. From the oxidation curves, the oxidation mass gain per unit area with time was of parabolic relation and oxidation rate slowed down. On the basis of experimental data, the isothermal oxidation kinetics model was derived and oxidation activation energy of SPHC steel was 127. 416 kJ/mol calculated from kinetics data.
|
Received: 18 June 2012
Published: 19 March 2014
|
Fund:National Science and Technology Planning Project;Fundamental Research Funds for the Chinese Central Universities |
|
|
|
[1] |
LI Sheng-cun. Discussion of the red rust on the surface of high Si high strength steel[J]. Chinese Journal of Iron and Steel, 2017, 35(5): 47-50. |
[2] |
FU Song-yue��REN Yong��CHENG Xiao-ru��WANG Hao��FAN Jing-guo��SHEN Jin-long. Descaling property of third oxide scale of high carbon steel wire[J]. Chinese Journal of Iron and Steel, 2016, 51(3): 73-77. |
[3] |
WANG Chang,YU Yang,WANG Lin,PANG Zai- gang,CHEN Jin,JIAO Hui- li. Effects of C and P on blistering behavior of scale of hot rolled strip[J]. Chinese Journal of Iron and Steel, 2016, 28(3): 74-79. |
[4] |
WEI Bing��HAN Bin��YANG Yi��LIU Yang��TAN Wen��WANG Shui-ze. Cause analysis of typical surface defect of hot-rolled ultra-low carbon steel[J]. Chinese Journal of Iron and Steel, 2016, 34(2): 42-46. |
[5] |
LIN Chong,LIU Hong-yu,,WANG Hong-jun,XU Hong-bing,LU Jian-duo. Formation of oxide scale on tire cord steel during isothermal holding and controlled cooling[J]. Chinese Journal of Iron and Steel, 2015, 27(6): 40-44. |
[6] |
ZHOU Peng��HUI Kai��ZANG Tao��JIN Sai-te. Analysis of oxide scales microstructure of hot rolled duplex stainless steel 2205 strip[J]. Chinese Journal of Iron and Steel, 2015, 50(5): 59-62. |
|
|
|
|