| Bainite Transformation of Low-carbon and Boron-containing Steel under Continuous Cooling |
| Zhi-hong ZHANG1,2,3,4,Xiang-xin XUE1,2,3,4 |
1. Institute of Metallurgical Resources and Environmental Engineering, Northeastern University, Shenyang 110819,Liaoning, China
2. Liaoning Key Laboratory of Metallurgical Resources Circulation Science, Shenyang 110819,Liaoning, China
3. Liaoning Engineering Technology Research Center of Comprehensive Utilization of Boron Resources, Shenyang 110819, Liaoning, China
4. Liaoning University Key Laboratories of Ecological Utilization Technology of Boron Resources and Boron Materials, Shenyang 110819, Liaoning, China |
|
|
|
|
Abstract The effects of deformation temperature and strain on bainite transformation of low carbon steel and boron-containing steel were investigated under continuous cooling conditions by means of dilatometric measurement and microstructure observation. The results show that with decreasing the deformation temperature from 1000 to 800 �� and increasing strains, bainite start temperature for boron-containing low carbon steel increases, whereas it decreases for low carbon steel under the same condition. The bainite microstructures are easily obtained for boron-containing steel deformed at different temperatures and different strains compared with plain low carbon steel. With increasing the continuous cooling rate, the bainite start temperature under deformed condition is about 20 �� higher than that under undeformed condition for boron-containing steel, but it changes slightly when the cooling rate is 20 ��/s or more.
|
|
Received: 16 July 2012
Published: 19 March 2014
|
|
Corresponding Authors:
Zhi-Hong ZHANG
E-mail: crespokaka@163.com
|
|
|
|
| [1] |
Ming-bo Zhou,Jing-lin Tang,*,Jie Yang,Cun-yu Wang. Tailored properties of a novelly-designed press-hardened 22MnMoB steel[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 508-512. |
| [2] |
Xuan-wei Lei,Ji-hua Huang*,Shu-hai Chen,Xing-ke Zhao. New bainite kinetics of high strength low alloy steel in fast cooling process[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 229-233. |
| [3] |
Hua Zhang,Yan-xin Wu,Jian-xun Fu*,Jie Xu,Qi-jie Zhai. Influence of on-line tempering parameters on microstructure of medium-carbon steel[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 59-66. |
| [4] |
Zheng-yun Zhang,Jian-chun Cao,*,Zhong-hua Zhong,Xiao-long Zhou,Wei Chen,Yin-hui Yang. Tensile deformation behavior of high strength anti-seismic steel with multi-phase microstructure[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 111-120. |
| [5] |
Hui GAO,Bang-shao DONG,Shao-xiong ZHOU. Advances in Investigation of Fe-based Glass-forming Alloy Melts[J]. Chinese Journal of Iron and Steel, 2016, 23(6): 509-515. |
| [6] |
Cun-jiang TANG,Shi-long LIU,Cheng-jia SHANG. Micromechanical Behavior and Failure Mechanism of F/B Multi-phase High Performance Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(5): 489-494. |
|
|
|
|
2014, Vol. 21 