| Effect of Hf and Zr Contents on Stress-rupture and Fatigue Crack Growth Rate Performances in FGH96 PM Superalloy |
| Tian XIA1,2,Yi-wen ZHANG1,2,Yue CHI1,2 |
1. High Temperature Materials Research Institute, Central Iron and Steel Research Institute, Beijing 100081, China
2. Beijing Key Laboratory of Advanced High Temperature Materials, Beijing 100081, China |
|
|
|
|
Abstract Four experimental FGH96 alloys with various contents of Hf and Zr (0 and 0. 04%, 0. 3% and 0. 04%, 0. 6% and 0. 04%, 0. 3% and 0. 06%, respectively) were produced using PREP (plasma rotating electrode process)+HIP (hot isostatic pressing) route. The unnotched and notched stress-rupture properties and fatigue crack growth rate (FCGR) of all the experimental alloys were investigated to study the effect of Hf and Zr. Relevant fracture morphology and microstructure were observed by scanning electron microscopy and transmission electron microscopy. The results revealed that appropriate content of Hf could lengthen stress-rupture life, eliminate notch sensitivity and slower FCGR. Microstructure analysis showed that the amount of �á� phase should be increased or decreased by adjusting Hf and Zr contents, and MC carbide and oxide coupled growth should be increased by adding Hf content, which caused oxycarbide to precipitate along grain boundary and strengthen the alloy. It was found that excessive Zr in Hf-containing FGH96 alloy had certain deleterious effects on stress-rupture property because there was strong Zr segregation at prior particle boundary, leaving a long chain of large-size oxides along the boundary. The optimal content of Hf and Zr in FGH96 alloy was 0. 6% and 0. 04%, respectively.
|
|
Received: 01 November 2012
Published: 19 March 2014
|
| Fund:National Basic Research Program of China |
|
|
|
| [1] |
LUO Yi-wa����GUO Han-jie����SUN Xiao-lin����. Precipitation behaviors of carbides in M42 high speed steel during ESR and forging[J]. Chinese Journal of Iron and Steel, 2017, 52(7): 68-75. |
| [2] |
XUE Peng��HE Dong-feng��XU An-jun��YANG Qi-xing��. Formation of MgFe2O4 and recycling of iron from modified BOF slag by magnetic separation[J]. Chinese Journal of Iron and Steel, 2017, 52(7): 104-108. |
| [3] |
WANG Dong-chen,LI Xiao-yuan,WEI Li-jin,SHI Jie,WANG Qi,XU Le. Effect of tempering temperature on fracture toughness of high carbon steel[J]. Chinese Journal of Iron and Steel, 2017, 29(6): 494-499. |
| [4] |
LI Xin-yu����YANG Mao-sheng��ZHOU Xiao-long��WANG Bo��. Influence of Co and Mo on microstructure and mechanical properties of bearing steel with high content of cobalt��chromium and molybdenum[J]. Chinese Journal of Iron and Steel, 2017, 52(5): 77-86. |
| [5] |
ZHANG Hong-liang����SHI Qi��LONG Hong-ming����LI Jia-xin��CHUN Tie-jun��GAO Zhi-fang. Analysis of [NOx]removal process in sintering flue gas[J]. Chinese Journal of Iron and Steel, 2017, 52(5): 100-106. |
| [6] |
HUANG Fei��ZHU Xing-jiang��ZHANG Xiao-li��WU Zhen��WANG Yue. Cause analysis of the fracture of 8Cr5MoV forged steel cold roll[J]. Chinese Journal of Iron and Steel, 2017, 35(4): 42-46. |
|
|
|
|
2014, Vol. 21 