| Constitutive Equations for Flow Behavior of Powder-forged Fe-0. 5C-2Cu Steel under Hot Compression |
| Biao GUO1,Sui-cai ZHANG2,Chang-chun GE1,2 |
1. School of Materials Science and Engineering, Southwest Jiaotong University, Chengdu 610031,Sichuan, China
2. Institute of Special Ceramics and Powder Metallurgy, School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
|
|
Abstract To investigate the hot deformation behavior of powder-forged (P/F) Fe-0. 5C-2Cu steel, the hot compression tests were conducted at temperatures ranging from 900 to 1000 �� and strain rates from 0. 1 to 10 s-1 using Gleeble-1500 thermal simulator. The true stress-true strain curves at different temperatures and strain rates of P/F steel were obtained. It is found that dynamic recovery only occurs as strain rate is 10 s-1 at 900 ��, and the dynamic recrystallization is the main softening mechanism. The flow stress increases with decreasing temperature and increasing strain rate. The experimental data are employed to develop constitutive equations on the basis of the Arrhenius-type equation by introducing the strain with nonlinear fitting. The flow stresses predicted by the proposed constitutive equations are in good agreement with the experimental values, and the correlation coefficient (R2) and the average absolute relative error (AARE) are 0. 99525 and 3. 07% respectively. These results indicate the proposed constitutive equations can effectively describe the hot deformation behavior of the material.
|
|
Received: 06 November 2012
Published: 19 March 2014
|
|
Corresponding Authors:
Biao GUO
E-mail: biaoguo_mse@126.com
|
|
|
|
| [1] |
ZHANG Shi-wei������YANG Ming������LIANG Yi-long������JIANG Yun����LONG Shao-lei����. Constitutive equations and dynamic recrystallization behaviors of 20CrNi2Mo steel at stage of high temperature deformation[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 97-105. |
| [2] |
GONG Qian-jiang��������LIANG Yi-long������ ��YANG Ming��������JIANG Yun��������XU Xiang������. Phenomenological constitutive model and dynamic recrystallization behavior of 20CrMnTiH steel[J]. Chinese Journal of Iron and Steel, 2017, 52(6): 67-75. |
| [3] |
LIANG Jian-xiong��YONG Qi-long��ZHANG Liang��WANG Chang-jun. Hot deformation behavior and its processing map of 1Cr17Ni1 duplex stainless steel[J]. Chinese Journal of Iron and Steel, 2016, 51(9): 82-89. |
| [4] |
WANG Ya-fen��DU Hong-zhi��ZHAO Guang-dong. Discussion of high strain rate test based on collision performance of steel for automobile[J]. Chinese Journal of Iron and Steel, 2016, 34(6): 24-27. |
| [5] |
WANG Zhe-ying,YU Xing-fu,QIAO He-ting. Hot deformation behaviors and microstructure of hot-rolled low-carbon steel[J]. Chinese Journal of Iron and Steel, 2016, 28(12): 59-66. |
| [6] |
CHEN Zheng- zong,LIU Zheng- dong,BAO Han- sheng. Corrected constitutive equation and processing maps of nickel- based heat- resistant alloy CN617 after hot compression test[J]. Chinese Journal of Iron and Steel, 2015, 27(9): 44-48. |
|
|
|
|
2014, Vol. 21 