Influence of Heat Treatment Temperature on Microstructure and Property of 00Cr13Ni5Mo2 Supermartensitic Stainless Steel |
De-ning ZOU1,Xiao-hua LIU1,Ying HAN2,Wei ZHANG3,Jiao LI1,Kun WU1 |
1. School of Metallurgy and Engineering, Xi��an University of Architecture and Technology, Xi��an 710055,Shaanxi, China 2. Key Laboratory of Advanced Structural Materials of Ministry of Education, Changchun University of Technology, Changchun 130012, Jilin, China 3. State Key Laboratory for Mechanical Behavior of Materials, Xi��an Jiaotong University, Xi��an 710049, Shaanxi, China |
|
|
Abstract The microstructural evolution and mechanical property of 00Cr13Ni5Mo2 supermartensitic stainless steel (SMSS) subjected to different heat treatments were investigated. Room tensile tests, hardness tests, scanning electron microscopy, transmission electron microscopy and X-ray diffraction were conducted on the heat-treated steels. It is found that the microstructure of the heat-treated steel is composed of tempered lath martensite, retained austenite and ��-ferrite. The austenitizing temperature and tempering temperature have a significant effect on the microstructural changes, which leads to the complex variations of mechanical properties. The fine tempered lath martensite and more dispersed reversed austenite in the microstructure facilitate improving the comprehensive mechanical properties of the studied steel. The optimal heat treatment process of 00Cr13Ni5Mo2 SMSS is obtained by austenitizing at 1000 �� for 0. 5 h+air cooling followed by tempering at 630 �� for 2 h+air cooling, where the excellent combination of tensile strength, elongation and hardness can be achieved.
|
Received: 12 December 2012
Published: 19 March 2014
|
|
|
|
[1] |
Ying Ci,*,Zhan-zhan Zhang. Simulation study on heat-affected zone of high-strain X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 966-973. |
[2] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
[3] |
Min-qiang Gao,Ying-dong Qu,Guang-long Li,Jun-hua You,Rong-de Li. Cementites decomposition of a pearlitic ductile cast iron during graphitization annealing heat treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 838-843. |
[4] |
Hong-ru Ren,Jin-tao Gao,Zhe Wang,Chong Li,Fu-qiang Wang,Zhan-cheng Guo. Evolution of microstructure, mechanical and magnetic properties of electrodeposited 50%Ni-Fe alloy foil after thermal treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 844-851. |
[5] |
Hang-wei Zhou,,Hui-qun Liu,,Dan-qing Yi,,Yu Xiao,,Xiao-long Zhao,Jian Wang,Qi Gao. Effect of �� phase on fatigue crack growth of Ti-6242 alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 811-822. |
[6] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
|
|
|
|