| Control over Mechanical Properties and Microstructure of BR1500HS Hot-stamped Parts |
| Bai-liang ZHUANG1,2,Zhong-de SHAN1,Chao JIANG1,Xin-ya LI1 |
1. State Key Laboratory of Advanced Forming Technology and Equipment of CAM, Beijing 100083, China
2. Jiangsu Institute, China Academy of Machinery Science and Technology, Changzhou 213164, Jiangsu, China |
|
|
|
|
Abstract The hot-stamping processing parameters are of critical importance in transforming ultra-high-strength steel (UHSS) into high-quality parts, which were studied by mechanical properties tests, metallographic observations and calculation analysis method based on hot stamping experiments and numerical simulation technology, the mechanical properties, thickness, dimensional accuracy, and microstructure of the hot-formed parts are analyzed to determine the influence of different processing parameters for UHSS parts formed from BR1500HS. The results indicate that the quenching time had the most significant impact on the mechanical properties of the parts, and longer quenching time resulted in better mechanical properties. In addition, the pressing speed had a significant influence on the thickness of the formed parts, and the part-opening temperature had the most significant effect on the dimensional accuracy of the parts. And to get hot-stamped parts with excellent quality, the optimum process conditions should be set as heating temperature of 930 ��, soaking time of 4 min, stamping force of 7 MPa, pressing speed of 75 mm/s, quenching time of 15 s, and water-flow rate of 1. 1 m/s.
|
|
Received: 24 September 2013
Published: 05 June 2014
|
| Fund:National Outstanding Youth Science Foundation of China;National Outstanding Youth Science Foundation of China |
|
Corresponding Authors:
zhuang
E-mail: 411836452@qq.com
|
|
|
|
| [1] |
Ying Ci,*,Zhan-zhan Zhang. Simulation study on heat-affected zone of high-strain X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 966-973. |
| [2] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
| [3] |
Hang-wei Zhou,,Hui-qun Liu,,Dan-qing Yi,,Yu Xiao,,Xiao-long Zhao,Jian Wang,Qi Gao. Effect of �� phase on fatigue crack growth of Ti-6242 alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 811-822. |
| [4] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
| [5] |
Wei-jun Hui,*,Na Xiao,Xiao-li Zhao,Yong-jian Zhang,Yu-feng Wu. Effect of vanadium on dynamic continuous cooling transformation behavior of medium-carbon forging steels[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 641-648. |
| [6] |
Yong-xing Jiao,Jian-sheng Liu*,Xing-wang Duan,Xiao-hua Zheng,Wen-wu He. Prediction of critical forging penetration efficiency for 06Cr19Ni9NbN steel by dynamic recrystallization[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 649-653. |
|
|
|
|
2014, Vol. 21 