CO2 Gasification Characteristics of High and Low Reactivity Cokes |
Bing GAO,Jian-liang ZHANG,Hai-bin ZUO,Cheng-lin QI,Yan RONG,Zhe WANG |
University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract In order to effectively utilize the high reactivity coke, the gasification characteristics of high and low reactivity cokes were investigated at 1100 ��. Low reactivity coke A and high reactivity coke B were chosen and charged into the reaction tube in two methods. The results indicated that the mass loss ratio of high reactivity coke in mixed cokes was more significant than that of single high reactivity coke in the middle stage of reaction. Nevertheless, the mass loss ratio of low reactivity coke in mixed cokes was less than that of single low reactivity coke. It was mainly attributed to gas diffusion and internal reaction of coke. When high and low reactivity cokes were mixed, the practical average mass loss ratio was nearly the same as the weighted average. The microscopic structures of coke indicated that with the increase of reaction time, the external and internal layers of low reactivity coke reacted more uniformly with CO2, whereas the reaction degree of external layer of high reactivity coke was obviously higher.
|
Received: 27 December 2012
Published: 01 August 2014
|
Fund:National Basic Research Program of China |
Corresponding Authors:
Bing GAO
E-mail: sjzgaobing@163.com
|
|
|
|
[1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
[2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
[3] |
WANG Hai-yang��ZHANG Jian-liang��WANG Guang-wei��LI Tao��JIANG Xi��. Feasibility research of injection of BF dust into melter gasifier of COREX[J]. Chinese Journal of Iron and Steel, 2017, 52(8): 29-34. |
[4] |
LONG Yue,,DU Pei-pei,,ZHANG Liang-jin,,LI Zhi-hui,, ,ZHANG Yu-zhu,. Impact of various factors on property and fiber-forming effect of centrifugal blast furnace slag fibers[J]. Chinese Journal of Iron and Steel, 2017, 29(7): 530-535. |
[5] |
HAN Wei-gang��LI Xiu-ping��LIU Jian-hua��ZHANG Chun-xia��ZHOU Ji-cheng��SHI Xin-yue. Temperature drop of hot metal during BF tapping in Shougang Jingtang[J]. Chinese Journal of Iron and Steel, 2017, 52(6): 13-17. |
[6] |
MA Fu-tao��ZHANG Jian-liang��LIU Yun-cai. BF burden distribution numerical simulation based on genetic algorithm[J]. Chinese Journal of Iron and Steel, 2017, 52(6): 18-25. |
|
|
|
|