| Effect of Boron Mud and CaF2 on Surface Tension and Density of CaO-SiO2-B2O3 Ternary Slag Systems |
| Li-li YANG1,2,Hong-ming WANG1,2,Xiang ZHU1,2,Gui-rong LI1,2 |
1. School of Materials Science and Engineering, Jiangsu University, Zhenjiang 212013, Jiangsu, China
2. Jiangsu Province Key Laboratory of High-End Structural Materials, Zhenjiang 212013, Jiangsu, China |
|
|
|
|
Abstract The effect of boron mud and CaF2, which were used as fluxing agents, on surface tension and density of CaO-SiO2-B2O3 ternary slag systems was investigated. The surface tension and density were measured by using the ring detachment method and Archimedean method, respectively. The results indicated that surface tension and density of the slag systems decreased with increasing temperature in the range of 1380-1480 ��. When 5%-10% CaF2 was employed as fluxing agent, the surface tension and density of slag were decreased with increasing CaF2 content, and the surface tension changed from 0.3 to 0.6 N/m, while the density changed from 3.4 to 4.1 g/cm3. However, when using 5%-10% boron mud as fluxing agent, the surface tension was enhanced, whereas the density decreased with the increase of boron mud content, and the variation range was 0.4-0.6 N/m for surface tension and 3.2-3.9 g/cm3 for the density. As a conclusion, using boron mud as fluxing agent to substitute for CaF2 did not cause significant changes in slag surface tension and density.
|
|
Received: 16 January 2013
Published: 01 August 2014
|
| Fund:Projects Sponsored by the National Natural Science Foundation of China |
|
Corresponding Authors:
WAGNG Hong-Ming
E-mail: whmlgr@sina.com
|
|
|
|
| [1] |
CAO Wen-quan��XU Hai-feng����ZHANG Ming-da��DONG Han��WENG Yu-qing. Research and development of a new hot rolled laminated structure[J]. Chinese Journal of Iron and Steel, 2016, 51(9): 1-10. |
| [2] |
YUAN Jing����WU Zhan-fang��XU Li-jun��ZHAO He-ming. Study on heat transfer coefficient of continuous water spray cooling for high temperature steel plate[J]. Chinese Journal of Iron and Steel, 2016, 41(3): 9-13. |
| [3] |
CHEN Jun-fu��HUANG Jian-yang��WAN En-tong��CAO Tong-you��YANG Cheng-wei�� PENG Zhu-gang. Effect of basicity on heat transfer performance of peritectic steel mold flux[J]. Chinese Journal of Iron and Steel, 2016, 41(2): 17-19. |
| [4] |
WANG Pu��SHI Zeng- min��ZHANG Yun- ti��YIN De- zheng��FENG Ping. Evolution of microstructure of 22SiMn2TiB steel during quenching- tempering process[J]. Chinese Journal of Iron and Steel, 2016, 28(2): 45-50. |
| [5] |
LI Shu-long,CHEN Ye-xin,YANG Biao. Effect of current density of dynamic hydrogen charging on mechanical properties of BG110S oil-well tubular[J]. Chinese Journal of Iron and Steel, 2016, 28(10): 63-68. |
| [6] |
WANG Kun-peng��JIANG Min��ZHAO Hao-qian��WANG Xin-hua��WANG Ying. Contrast on non-metallic inclusions control in wire rods for saw wire[J]. Chinese Journal of Iron and Steel, 2016, 51(1): 33-38. |
|
|
|
|
2014, Vol. 21 