Magnetic Properties of FeSiBC Amorphous Alloy Powder Cores Using Mechanical-crushed Powder |
Xiang-yue WANG1,2,Zhi-chao LU1,2,Cao-wei LU1,2,Guang-min LI2,De-ren LI1,2 |
1. China Iron and Steel Research Institute, Beijing 100081, China 2. Advanced Technology and Materials Co., Ltd., Beijing 100081, China |
|
|
Abstract The FeSiBC amorphous powder cores were fabricated using powders of the FeSiBC amorphous ribbons which were mechanically crushed for a short time, and the relationship between magnetic properties and powder particle sizes was evaluated. The saturation magnetization Bs of the amorphous Fe82Si2B15C1 alloy was 1.62 T, which provided a superior dc-bias property for the powder cores. Meanwhile, a stable permeability up to high frequency range over 10 MHz and the low core loss of 400 kW/m3 at f=50 kHz and Bm=0.1 T were obtained. These excellent high-frequency magnetic properties of the FeSiBC amorphous powder cores could be attributed to the effective electrical insulation between the FeSiBC amorphous powders made by mechanical crushing.
|
Received: 28 January 2013
Published: 13 November 2014
|
Corresponding Authors:
Xiang-Yue
E-mail: 251597916@qq.com
|
|
|
|
|
|
|