Microstructure and Mechanical Properties of Ductile Cast Iron in Lost Foam Casting with Vibration |
Bo-tao XIAO1,2,Zi-tian FAN1,Wen-ming JIANG1,3,Xin-wang LIU1,Wei LONG1,Qiang HU1,4 |
1. State Key Laboratory of Material Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan 430074, Hubei, China 2. School of Materials Science and Engineering, Jiangxi Science and Technology Normal University, Nanchang 330013, Jiangxi, China 3. School of Mechanical �� Electrical Engineering,Wuhan Institute of Technology, Wuhan 430073, Hubei, China 4. Jiangxi Key Laboratory for Advanced Copper and Tungsten Materials, Jiangxi Academy of Sciences, Nanchang 330029, Jiangxi, China |
|
|
Abstract The microstructures and mechanical properties of the ductile cast iron (DI) specimens obtained by lost foam casting (LFC) with and without vibration were investigated. The results indicate that the number of the graphite nodule increases from 175 mm-2 of the specimens produced by LFC without vibration to 334 mm-2 of the specimens produced by LFC with vibration, and the thickness of the ferrite shell increases. Meanwhile, the amount of the carbides decreases in the specimens produced by LFC with vibration and the granule structure then forms. These are mainly attributed to the ��crystal shower�� caused by the vibration. In addition, the tensile strength and elongation of DI specimens produced by LFC with vibration are improved due to the dispersion-strengthening of refined carbide and pearlite colony, uniform distribution of the graphite nodule, and increase of the amount of dimples and tearing edges.
|
Received: 27 May 2013
Published: 13 November 2014
|
Corresponding Authors:
Bo-Tao XIAO
E-mail: xltao_2005@163.com
|
|
|
|
[1] |
Ying Ci,*,Zhan-zhan Zhang. Simulation study on heat-affected zone of high-strain X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 966-973. |
[2] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
[3] |
Hang-wei Zhou,,Hui-qun Liu,,Dan-qing Yi,,Yu Xiao,,Xiao-long Zhao,Jian Wang,Qi Gao. Effect of �� phase on fatigue crack growth of Ti-6242 alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 811-822. |
[4] |
Reng-chong Xu,,Yan-lin He,,Hu Jiang,,Hua Wang,,Na-qiong Zhu,,Xiao-gang Lu,, Lin Li,. Microstructures and mechanical properties of ferrite-based lightweight steel with different compositions[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 737-742. |
[5] |
Wei-jun Hui,*,Na Xiao,Xiao-li Zhao,Yong-jian Zhang,Yu-feng Wu. Effect of vanadium on dynamic continuous cooling transformation behavior of medium-carbon forging steels[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 641-648. |
[6] |
Yong-xing Jiao,Jian-sheng Liu*,Xing-wang Duan,Xiao-hua Zheng,Wen-wu He. Prediction of critical forging penetration efficiency for 06Cr19Ni9NbN steel by dynamic recrystallization[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 649-653. |
|
|
|
|