| Flow Stress Behaviors and Microstructure Evolution of 300M High Strength Steel under Isothermal Compression |
| Rong-sheng QI,Bao-feng GUO,Xin-gang LIU,Miao JIN |
| Key Laboratory of Advanced Forging & Stamping Technology and Science Yanshan University, Ministry of Education of China, Qinhuangdao 066004, Hebei, China |
|
|
|
|
Abstract The compressive deformation behaviors of 300M high strength steel were investigated over a wide range of temperatures (850-1200 ��) and strain rates (0. 001-10 s-1) on a Gleeble-3800 thermo-mechanical simulator. The measured flow stress was modified by the corrections of the friction and the temperature compensations, which nicely reflect negative effects of the friction and temperature on the flow stress. The corrected stress-strain curves were the dynamic recrystallization type on the conditions of higher deformation temperature and lower strain rate. Flow stress increases with the increase of strain rate at the same deformation temperature and strain. By contrast, flow stress decreases with the increase of temperature at the same strain rate and strain. Dependence of the peak stress on temperature and strain rate for 300M steel is described by means of the conventional hyperbolic sine equation. By regression analysis, the activation energy (Q) in the whole range of deformation temperature is determined to be 367. 562 kJ/mol. The effects of the temperature and the strain rate on microstructural evolution are obvious. With the increase of the deformation temperature and the decrease of the strain rate, the original austenite grain sizes of 300M steel increase. At the same time, the corrected flow stress curves more accurately determine the evolution of the microstructure.
|
|
Received: 28 October 2013
Published: 04 December 2014
|
| Fund:Technology Major Projects of;atural Science Research Foundation Program for Distinguished Young Scholars in Higher Education Institutions of Hebei Province, China |
|
Corresponding Authors:
Rong-Sheng QI
E-mail: comehomer@163.com
|
|
|
|
| [1] |
Yang Yun,Qing-wu Cai,,Bao-sheng Xie,*,Shuang Li. Effect of tempering temperature on strain hardening exponent and flow stress curve of 1000 MPa grade steel for construction machinery[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 950-956. |
| [2] |
Yuan-ji Shi,Lan-ji Liu,Lei Zhang,Li-jun Zhang,Li Zheng,Run-xia Li,Bao-yi Yu*. Effect of squeeze casting process on microstructures and flow stress behavior of Al-17.5Si-4Cu-0.5Mg alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 957-965. |
| [3] |
Yong-xing Jiao,Jian-sheng Liu*,Xing-wang Duan,Xiao-hua Zheng,Wen-wu He. Prediction of critical forging penetration efficiency for 06Cr19Ni9NbN steel by dynamic recrystallization[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 649-653. |
| [4] |
Da-shan Sui,*,Hai-ming Zhang,Hong-yang Zhu,Zhe Zhu,Zhen-shan Cui. Effects of process parameters on fragment and refinement of millimeter-grade coarse grains for 316LN steel during hot cogging[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 529-535. |
| [5] |
Lei Wang,Di Tang*,Yong Song. Prediction of mechanical behavior of ferrite-pearlite steel[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 321-327. |
| [6] |
Hong��bin LI,,Yun��li FENG,Tao YAN,En��lin YU. Constitutive Model of Warm Deformation Behavior of Medium Carbon Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(9): 940-948. |
|
|
|
|
2014, Vol. 21 