| 3D Thermo-mechanical Coupled Simulation of Whole Rolling Process for 60 kg/m Heavy Rail |
| Nuan-nuan PEI1,Guo-ming ZHU1,Bo LI1,Gong-ming TAO2,Yong-lin KANG1 |
1. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083,China
2. Pangang Group Panzhihua Steel & Vanadium Co. , Ltd. , Panzhihua 617062, Sichuan, China |
|
|
|
|
Abstract 3D thermo-mechanical coupled simulation of whole rolling process for 60 kg/m heavy rail was accomplished by FEM method. The finite element model, physical parameters of U75V and parameter setting of simulation were introduced in detail. The whole rolling process of 60 kg/m heavy rail was divided into 27 time cells to simulate respectively, and the model rebuilding and temperature inheritance method in intermediate pass were proceeded. Then, based on simulation results, the workpiece deformation result, metal flow, stress and strain of 60 kg/m heavy rail for typical passes were obtained. The temperature variation curves of whole rolling process for section key points of 60 kg/m heavy rail were plotted, and the temperature falling law of whole rolling process for 60 kg/m heavy rail was studied. In addition, temperature distribution of 60 kg/m heavy rail after whole rolling process was analyzed, and the results showed that temperature was highest at center of rail head and lowest at fringe of rail base. Moreover, the simulation results and measured results of rolling force for 60 kg/m heavy rail were compared, and the regularity was in good agreement.
|
|
Received: 14 May 2013
Published: 04 December 2014
|
|
|
|
| [1] |
Yang Yun,Qing-wu Cai,,Bao-sheng Xie,*,Shuang Li. Effect of tempering temperature on strain hardening exponent and flow stress curve of 1000 MPa grade steel for construction machinery[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 950-956. |
| [2] |
Ying Ci,*,Zhan-zhan Zhang. Simulation study on heat-affected zone of high-strain X80 pipeline steel[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 966-973. |
| [3] |
Qiu-lin Niu,,Wei-wei Ming,Ming Chen,Si-wen Tang,,Peng-nan Li,. Dynamic mechanical behavior of ultra-high strength steel 30CrMnSiNi2A at high strain rates and elevated temperatures[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 724-729. |
| [4] |
Wan-ming Li,Zhou-hua Jiang,,*,Xi-min Zang,Xin Deng. Modeling of flow and temperature distribution in electroslag remelting withdrawal process for fabricating large-scale slab ingots[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 569-578. |
| [5] |
Long Guo,Xing-zhong Zhang*,Chang-xi Feng. Continuous bending and straightening technology of Q345c slab based on high-temperature creep deformation[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 595-600. |
| [6] |
Qian-qian Ren,,Yu-zhu Zhang,,*,Yue Long,Shao-sheng Chen,Zong-shu Zou,Jie Li, Chen-guang Xu. Crystallization behavior of blast furnace slag modified by adding iron ore tailing[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 601-607. |
|
|
|
|
2014, Vol. 21 