| Response Characteristics and Adiabatic Heating during High Strain Rate for TRIP Steel and DP Steel |
| Yi GAO,Chao XU,Zhong-ping HE,Yan-lin HE,Lin LI |
| School of Materials Science and Engineering, Shanghai University, Shanghai 200072, China |
|
|
|
|
Abstract By using a static and high-speed material testing machine, tensile deformation behaviors of two kinds of Si-Mn TRIP (transformation induced plasticity) steels and DP (dual phase) steel were studied in a large range of strain rates (0.001-2000 s-1). Temperature variation during adiabatic heating and the amount of retained austenite at fracture were measured by an infrared thermometer and an X-ray stress analyser, respectively. The microstructure of steels was observed by optical microscopy (OM) and scanning electron microscopy (SEM) before and after tensile test. It was found from the experimental results that the tensile strength of these steels increased, and the fracture elongation firstly decreased and subsequently increased, as the strain rate increased in the range of 0.1-2000 s-1. The temperature raised during adiabatic heating of TRIP steel was in the range of 100-300 ��, while that of the DP steel was in the range of 100-220 ��. The temperature rise of these steels increased with increasing the strain rate, as well as the amount of the transformed retained austenite in TRIP steels. It was confirmed that austenite to martensite transformation is not suppressed by adiabatic heating.
|
|
Received: 29 September 2013
Published: 05 January 2015
|
| Fund:National Outstanding Youth Science Foundation of China;National Outstanding Youth Science Foundation of China;National Outstanding Youth Science Foundation of China |
|
Corresponding Authors:
Chao
E-mail: xugao_88@sina.com
|
|
|
|
| [1] |
Xiao-li Zhao,,Yong-jian Zhang,Cheng-wei Shao,Wei-jun Hui,Han Dong. Thermal stability of retained austenite and mechanical properties of medium-Mn steel during tempering treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 830-837. |
| [2] |
Qiu-lin Niu,,Wei-wei Ming,Ming Chen,Si-wen Tang,,Peng-nan Li,. Dynamic mechanical behavior of ultra-high strength steel 30CrMnSiNi2A at high strain rates and elevated temperatures[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 724-729. |
| [3] |
Long Guo,Xing-zhong Zhang*,Chang-xi Feng. Continuous bending and straightening technology of Q345c slab based on high-temperature creep deformation[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 595-600. |
| [4] |
Jiao-jiao Li,Jun-wei Qiao,,*,Karin A. Dahmen,Wei-ming Yang,Bao-long Shen5,Ming-wei Chen6. Universality of slip avalanches in a ductile Fe-based bulk metallic glass[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 366-371. |
| [5] |
Hui Guo,Peng Zhou,*,Ai-min Zhao,,Chao Zhi,Ran Ding,Jia-xing Wang. Effects of Mn and Cr contents on microstructures and mechanical properties of low temperature bainitic steel[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 290-295. |
| [6] |
Ji-bo Peng,,Hu Jiang,,Gong-ting Zhang,Li-ben Chen,,Na-qiong Zhu,,Yan-lin He,,*, Xiao-gang Lu,,Lin Li,. In-situ analysis of retained austenite transformation in high-performance micro-alloyed TRIP steel[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 313-320. |
|
|
|
|
2015, Vol. 22 