Effect of V and N on Microstructures and Properties of Grade-70 Tire Cord Steel during Cold Drawing |
Hong-yu LIU1,2,Bao-yi WAN1,Xiao-yu ZENG3,Chong LIN1,Hong-jun WANG1 |
1. College of Science,Wuhan University of Science and Technology, Wuhan 430065, Hubei, China 2. Hubei Province Key Laboratory of Systems Science in Metallurgical Process, Wuhan 430065, Hubei, China 3. Department of Physics and Astronomy, Clemson University, Clemson 29634, South Carolina, USA |
|
|
Abstract Commercial grade-70 tire cord steel was microalloyed with V and N to explore the possibility of substituting V for C and the effect of V and N on cementite dissolution during cold drawing process. Tensile strength, elongation and torsion laps of cold-drawn wires were determined. Microstructures of secondary phases were studied by transmission electron microscopy (TEM) and energy dispersive spectroscopy (EDS). Saturation magnetization was measured by using a vibrating sample magnetometer (VSM) to evaluate cementite dissolution during cold drawing process. Experimental results showed that with the increase of V content, tensile strength increased, elongation slightly decreased, and the torsion laps of the cold-drawn wires decreased. Results also showed that with the increase of N content, a peak (increasing first and then decreasing) appeared in the tensile strength graph, and an increase of elongation and a decrease of torsion laps of the cold-drawn wires occured. N is soluble in ferrite when its content is low. The increase in the content of N to 82��10-6 will result in the precipitation of the V-containing secondary phases. Also, cementite tended to be stable during cold drawing process with the increase of V and N contents. Grade-80 tire cord steel can be replaced by grade-70 tire cord steel microalloyed with 0. 086 mass% V.
|
Received: 21 November 2013
Published: 02 February 2015
|
Corresponding Authors:
Hong-Yu Liu
E-mail: liuhongyu@wust.edu.cn
|
|
|
|
[1] |
Wei-jun Hui,*,Na Xiao,Xiao-li Zhao,Yong-jian Zhang,Yu-feng Wu. Effect of vanadium on dynamic continuous cooling transformation behavior of medium-carbon forging steels[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 641-648. |
[2] |
Cheng-song Liu,Xiao-qin Liu,*,Hong-wei Ni,Shu-feng Yang,Jing-she Li,Fei Ye. Effect of vanadium on modification of inclusions in Mn- and Si-deoxidized steel during heat treatment at 1473 K[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 520-528. |
[3] |
Zhi-gang Song*,Han Feng,Shao��mei Hu. Development of Chinese duplex stainless steel in recent years[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 121-130. |
[4] |
Hai-feng Xu,,*,Feng Yu,Chang Wang,Wan-li Zhang,Jian Li,Wen-quan Cao. Comparison of microstructure and property of high chromium bearing steel with and without nitrogen addition[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 206-213. |
[5] |
Wei Li,Gui-qin Fu,Man-sheng Chu,Miao-yong Zhu*. Reduction behavior and mechanism of Hongge vanadium titanomagnetite pellets by gas mixture of H2 and CO[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 34-42. |
[6] |
Ji-chun Yang,Xiang-jun Liu,Gui-xiao Jia*,Xiao-yang Fu. A first-principles study on electronic structures and elastic properties of metal doped ��-Fe(N) high nitrogen steel[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 103-110. |
|
|
|
|