Combination Effect of Si and P on Tertiary Scale Characteristic of Hot Rolled Strip |
Yang YU1,Chang WANG1,Lin WANG1,Jin CHEN2,Ya-jun HUI1,Chang-ku SUN1 |
1. Sheet Metal Research Institute, Shougang Research Institute of Technology, Beijing 100043, China 2. Department of Technology and Quality, Shougang Qian��an Iron and Steel Co., Ltd., Qian��an 064404, Hebei, China |
|
|
Abstract For high strength interstitial free (IF) steel containing P element, the salt and pepper (SP) defects exist on the strip surface and could not be eliminated effectively by optimizing the hot rolling process, such as temperature and cooling water. The combination effect of Si and P on the characteristic of tertiary scale has been studied comprehensively by scanning electron microscopy (SEM) and electron probe microanalysis (EPMA), and the concept is proposed firstly that Si and P are of combination effect which can be utilized to eliminate the SP defect. The results show that the SP defects were induced by the rolled-in scale during finish rolling. P can be enriched at the interface between substrate and tertiary scale, which is easy to decrease the adhesion of tertiary scale. However, Si enrichment at the interface between substrate and tertiary scale can increase the adhesion. The SP defects can be eliminated completely, which is attributed to the accompanying enrichment of Si and P.
|
Received: 05 December 2013
Published: 06 March 2015
|
Corresponding Authors:
Yang YU
E-mail: yyhpd@163.com
|
|
|
|
[1] |
Jos�� Angel BARRIOS,C��sar VILLANUEVA,Alberto CAVAZOS,Rafael COL��S. Fuzzy C-means Rule Generation for Fuzzy Entry Temperature Prediction in a Hot Strip Mill[J]. Chinese Journal of Iron and Steel, 2016, 23(2): 116-123. |
[2] |
Wei-gang LI,Chao LIU,Ning FENG,Xi CHEN,Xiang-hua LIU. Friction Estimation and Roll Force Prediction during Hot Strip Rolling[J]. Chinese Journal of Iron and Steel, 2016, 23(12): 1268-1276. |
[3] |
Xiao-chen WANG,Quan YANG,You-zhao SUN. Rectangular Section Control Technology for Silicon Steel Rolling[J]. Chinese Journal of Iron and Steel, 2015, 22(3): 185-191. |
[4] |
Yan-zhao LUO,Jiong-ming ZHANG,Qiang LIU,Mao-kang LI,Yi-tong HAN,Yi-fei CAO. Evolution of Surface Transversal Crack in Intermediate Slabs during Hot Rolling Deformation[J]. Chinese Journal of Iron and Steel, 2014, 21(4): 476-481. |
[5] |
Ai-hua CHEN,Hai-rong GUO,Hua-long LI,Toshihiko EMI. Formation of Edge Crack in 1��4%Si Non-oriented Electrical Steel during Hot Rolling[J]. Chinese Journal of Iron and Steel, 2014, 21(2): 269-274. |
[6] |
CHEN Yin-li,SU Lan,ZHAO Ai-min,KUAI Zhen,LI Ben-hai,LIU Guang-ming. Effects of Rolling Parameters on Texture and Formability of High Strength Ultra-Low Carbon BH Steel[J]. Chinese Journal of Iron and Steel, 2013, 20(6): 75-81. |
|
|
|
|