| Abrasive Wear Resistance of Dual Phase Steels DP980 and DP600 |
| Xiu-lin JI1,Ju-yi WANG1,Cui-cui JI2,Jian-hua ZHAO2 |
1. Engineering Research Center of Dredging Technology of Ministry of Education, Hohai University, Changzhou 213022, Jiangsu, China
2. College of Mechanical and Electrical Engineering, Hohai University, Changzhou 213022, Jiangsu, China |
|
|
|
|
Abstract The abrasive wear resistance of dual phase(DP) steels DP980 and DP600 was investigated by using an ASTM rubber wheel abrasion tester. At 2.40 m��s-1 sliding speed under 19.9 N load with 180-355 ��m abrasive sands, the wear rates of DP980 and DP600 were 1.01��10-11 and 0.86��10-11 m3��m-1, respectively, corresponding to about 1.9 and 2.3 times of the relative wear resistance of normal low-carbon steel ASTM A283C. Using directly water quenching from austenitic temperature, the abrasive wear resistance of DP980 samples under 19.9 N load could be improved by 1.65 times. The wear rates of DP980 and DP600 samples decreased respectively with increasing sliding speed and abrasive particle size and decreasing applied load. The experimental results reveal that the effect of martensite on the wear resistance not only depends on the volume fraction but also depends on the morphology, distribution and grain size.
|
|
Received: 16 December 2013
Published: 13 April 2015
|
| Fund:the Fundamental Research Funds for the Central Universities of China |
|
Corresponding Authors:
Xiulin Ji
E-mail: xiulinji@gmail.com
|
|
|
|
| [1] |
Min-qiang Gao,Ying-dong Qu,Guang-long Li,Jun-hua You,Rong-de Li. Cementites decomposition of a pearlitic ductile cast iron during graphitization annealing heat treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 838-843. |
| [2] |
Hong-ru Ren,Jin-tao Gao,Zhe Wang,Chong Li,Fu-qiang Wang,Zhan-cheng Guo. Evolution of microstructure, mechanical and magnetic properties of electrodeposited 50%Ni-Fe alloy foil after thermal treatment[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 844-851. |
| [3] |
Tao Zhang,,Cheng-yong Wang,*,Lugee Li,**,Yong Zhang,Cui-lan Liu. Mass production of magnetocaloric LaFeMnSiB alloys with hydrogenation[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 462-468. |
| [4] |
Zi-long Qiu,Zhi-guo Luo,*,Heng Zhou,Ren Chen,Feng Wang,Zong-shu Zou. Effect of screw casing structure on descending of burdens in COREX shaft furnace[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 18-26. |
| [5] |
Dong-dong Zhuang,*,Lei-gang Wang,Yao Huang,Xiao-min Li,Hua-yang Zhang,De-wei Ren. Microstructure and texture evolution during recrystallization of low-carbon steel sheets[J]. Chinese Journal of Iron and Steel, 2017, 24(1): 84-90. |
| [6] |
Shi-guang PENG,Ren-bo SONG,Zhi-dong TAN,Chang-hong CAI,Ke GUO,,Zhong-hong WANG. Abrasive Wear Behaviors of Light-weight Austenitic Fe-24Mn-7Al-1C Steel and Mn13Cr2 Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 857-866. |
|
|
|
|
2015, Vol. 22 