Critical Heat Flux of Blast Furnace Hearth in China |
Yang-long LI1,2,Shu-sen CHENG1,2,Chuan CHEN1,2 |
1. School of Metallurgical and Ecological Engineering, University of Science and Technology Beijing,Beijing 100083, China 2. State Key Laboratory of Advanced Metallurgy, University of Science and Technology Beijing, Beijing 100083, China |
|
|
Abstract The critical heat flux surveys of thirteen Chinese blast furnaces were carried out. The mathematical model of hearth bottom was established and the temperature field was simulated by utilizing the method of inverse problem based on the collected parameters and temperature data. The critical heat flux and dangerous critical heat flux of hearth were defined and analyzed as well as the initial and investigative critical heat flux of hearth, and the influences of thermal conductivity and residual thickness of carbon bricks on critical heat flux were discussed. The relationships between critical heat flux of stave and hearth bricks were also compared. It is found that the dangerous critical heat flux of these blast furnaces ranged from 9.38 to 57 kW/m2. Therefore, there was no uniform critical heat flux of hearth due to the structure design, refractory materials selection, construction quality of hearth and other factors. The heat flux should be lower than the critical heat flux with corresponding thickness of carbon bricks to control the erosion of hearth. The critical heat flux of stave would be much lower than that of hearth bricks with the air gap. However, the critical heat flux of stave should be higher than that of hearth bricks when gas existed between furnace shell and staves.
|
Received: 14 October 2013
Published: 07 May 2015
|
Corresponding Authors:
Yang-Long LI
E-mail: yanglong.xlnm@163.com
|
|
|
|
[1] |
Yu-cheng Lei,,*,Xiao-kai Guo,Hong-xia Chang,Tian-qing Li,,Qiang Zhu,Gang Chen, Long-ren Xiao. Cavitation erosion behavior of CLAM steel weld joint in liquid lead-bismuth eutectic alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 935-942. |
[2] |
Hong-tao Wang,Wei Zhao,Man-sheng Chu,Cong Feng,Zheng-gen Liu,Jue Tang. Current status and development trends of innovative blast furnace ironmaking technologies aimed to environmental harmony and operation intellectualization[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 751-769. |
[3] |
Wei Zhang,,Zheng-liang Xue,Ju-hua Zhang,Wei Wang,Chang-gui Cheng,Zong-shu Zou. Medium oxygen enriched blast furnace with top gas recycling strategy[J]. Chinese Journal of Iron and Steel, 2017, 24(8): 778-786. |
[4] |
Qian-qian Ren,,Yu-zhu Zhang,,*,Yue Long,Shao-sheng Chen,Zong-shu Zou,Jie Li, Chen-guang Xu. Crystallization behavior of blast furnace slag modified by adding iron ore tailing[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 601-607. |
[5] |
Xue-feng She,*,Xiu-wei An,Jing-song Wang,Qing-guo Xue,Ling-tan Kong. Numerical analysis of carbon saving potential in a top gas recycling oxygen blast furnace[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 608-616. |
[6] |
Xun-fu Wang,,Qi-jie Zhai. Corrosion mechanism research and microstructure analysis of Baosteel No��3 blast furnace hearth[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 1016-1022. |
|
|
|
|