High Temperature Low Cycle Fatigue Behavior of GH4742 Alloy |
He-yong QIN1,Gang CHEN2,Qiang ZHU2,Chuan-jie WANG2,Peng ZHANG2 |
1. Central Iron and Steel Research Institute, Beijing 100081, China 2. School of Materials Science and Engineering, Harbin Institute of Technology at Weihai, Weihai 264209, Shandong, China |
|
|
Abstract High temperature low cycle fatigue tests on GH4742 superalloy were studied under the total strain-controlled conditions at 650 ��. Combined with fatigue test data, fatigue properties of the alloy were analyzed. Fracture morphology and dislocation structure were observed by scanning electron microscopy and transmission electron microscopy. The results showed that fatigue life and fatigue resistance of GH4742 alloy decreased significantly with increasing total strain amplitude. The cyclic hardening, cyclic softening and cyclic stability phenomena of the alloy occurred during the low cycle fatigue process. The increasing total strain amplitude is conducive to the formation of �á� phase. Fatigue crack propagation is controlled jointly by ductile and brittle fracture. Inhomogeneous deformation and deformation restricted in slip bands are the main reasons for the reduction of fatigue life of GH4742 alloy.
|
Received: 14 May 2014
Published: 05 June 2015
|
Fund:Major National Science and Technology Project of High-End CNC Machine Tools and Basic Manufacturing Equipments |
Corresponding Authors:
ZHANG Peng
E-mail: pzhang@yeah.net
|
|
|
|
[1] |
Zhao-xia Shi,,*,Xiao-feng Yan,Chun-hua Duan,Jin-gui Song,Ming-han Zhao,Jue Wang. Hot deformation behavior of GH4945 superalloy using constitutive equation and processing map[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 625-633. |
[2] |
Shu-lin Tan,Kun Yang,,Ya-nan Ding,Xian-hong Han,,*. Fracture morphologies of a hot stamped steel and comparisons with several sheet metals[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 634-640. |
[3] |
Zhen-xue Shi,Shi-zhong Liu,Xiao-dai Yue,Li-jie Hu,Wan-peng Yang,Xiao-guang Wang,Jia-rong Li. Effect of cellular recrystallization on tensile properties of a nickel-based single crystal superalloy containing Re and Ru[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 1059-1064. |
[4] |
Li-ming TAN,,Yi-wen ZHANG,,Jian JIA,,Shou-bo HAN,. Precipitation of �� Phase in Nickel-based Powder Metallurgy Superalloy FGH97[J]. Chinese Journal of Iron and Steel, 2016, 23(8): 851-856. |
[5] |
Xue-li GAO,Jun-ying MIN,Ling ZHANG,Quan-chao LI,Chang-wei LIAN,,Jian-ping LIN. Prediction and Experimental Validation of Forming Limit Curve of a Quenched and Partitioned Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(6): 580-585. |
[6] |
Zhen-xue SHI,Shi-zhong LIU,Jian YU,Jia-rong LI. Tensile Behavior of the Second Generation Single Crystal Superalloy DD6[J]. Chinese Journal of Iron and Steel, 2015, 22(8): 738-742. |
|
|
|
|