Corrosion Behavior of S450EW Low-alloy Weathering Steel inCyclically Alternate Corrosion Environments |
Jun-shan WANG1,2, Pei-yang SHI1, Cheng-jun LIU1, Mao-fa JIANG1 |
1. Key Laboratory of Ecological Metallurgy of Multimetallic Mineral, Northeastern University, Shenyang 110819, Liaoning, China 2. Ansteel Group Co., Ltd., Anshan 114014, Liaoning, China |
|
|
Abstract Weathering steel is widely used in various fields due to its excellent mechanical properties and high corrosion resistance. The effect of chromium content on the S450EW weathering steel in cyclic immersion test was studied. The results indicated that the corrosion resistance of S450EW weathering steel is closely related to chromium content. The addition of chromium significantly inhibited the weathering steel corrosion. The corrosion rate of experimental steel after 96 h immersion was 1.101 g��m.2��h.1. The rust of S450EW weathering steel was mainly constituted of FeOOH and Fe3O4 phase, and the elevation of chromium content promoted the formation of ��-FeOOH. The fine precipitates of the two phases contributed to the formation of dense dust layer of test steel. Furthermore, the increase of chromium is beneficial for the cure of original defects and cracks of the rust layer via the enrichment of chromium. The corrosion potential and the resistance of corrosion process were thus increased, protecting the experimental steel from further corrosion. A S450EW steel with corrosion resistance more than 1.5 times of Q450NQR1 steel was prepared.
|
Received: 03 September 2014
Published: 09 November 2015
|
Fund:weathering steel; cyclic immersion test; rust structure; chromium;National Natural Science Foundation of China;Program for New Century Excellent Talents in University of Ministry of Education of China;Natural science Foundation of Liaoning Province of China |
Corresponding Authors:
Junshan Wang
E-mail: wangjs@ansteel.com.cn
|
|
|
|
[1] |
Zi-long Zhao,,Xue-gang Xing,Yi Luo,Yi-de Wang,,Wei Liang,*. Influence of Al-Si additions on mechanical properties and corrosion resistance of Mg-8Li dual-phase alloys[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 426-429. |
[2] |
Wen-juan Ge,Xu-ting Li,Peng Li,Peng-chao Qiao,Jian-wei Du,Shuai Xu,Yan Wang*. Microstructures and properties of CuZrAl and CuZrAlTi medium entropy alloys prepared by mechanical alloying and spark plasma sintering[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 448-454. |
[3] |
Long-hu Cao,Cheng-jun Liu*,Qing Zhao,Mao-fa Jiang. Effect of Al2O3 modification on enrichment and stabilization of chromium in stainless steel slag[J]. Chinese Journal of Iron and Steel, 2017, 24(3): 258-265. |
[4] |
Hai-feng Xu,,*,Feng Yu,Chang Wang,Wan-li Zhang,Jian Li,Wen-quan Cao. Comparison of microstructure and property of high chromium bearing steel with and without nitrogen addition[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 206-213. |
[5] |
Chao Geng,,Hua-jun Wang,*,Wen-tao Hu,Li Li,Cheng-shuai Shi. Recovery of iron and copper from copper tailings by coal-based direct reduction and magnetic separation[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 991-997. |
[6] |
Zhi-feng Li,Yong-quan He,Guang-ming Cao,Jun-jian Tang,Xiang-jun Zhang,Zhen-yu Liu. Effects of Al contents on microstructure and properties of hot-dip Zn-Al alloy coatings on hydrogen reduced hot-rolled steel without acid pickling[J]. Chinese Journal of Iron and Steel, 2017, 24(10): 1032-1040. |
|
|
|
|