| Effect of Subcritical Annealing Temperature on Microstructure and Mechanical Properties of SCM435 Steel |
| Cheng JI, Lei WANG, Miao-yong ZHU |
| School of Materials and Metallurgy, Northeastern University, Shenyang 110819, Liaoning, China |
|
|
|
|
Abstract The effect of subcritical annealing temperature on microstructure and mechanical properties of SCM435 steel was investigated through changing the heating and soaking temperature as 660 ��C, 680 ��C, 700 ��C, 720 ��C and 745 ��C. The microstructure and mechanical properties of intercritically annealed specimens were analyzed. With increasing the subcritical annealing temperature from 660 ��C to 720 ��C, the spheroidization ratio gradually increased, and the mechanical properties, formability and Vickers hardness were improved. According to the comprehensive comparison of mechanical properties and formability, the subcritical process at soaking temperature of 680.720 ��C could achieve similar annealing effect as that of intercritical process. Therefore, the subcritical annealing temperature could be set as 700 ��C in practice, with the Ac1 temperature fluctuation within ��20 ��C, and the applicability and stability of subcritical annealing were guaranteed in industrial application. The plant results of the cold heading showed that the subcritical annealing could replace original intercritical annealing successfully with significantly saving time and energy.
|
|
Received: 01 June 2015
Published: 09 November 2015
|
| Fund:National Natural Science Foundation of China;Fundamental Research Funds for the Central Universities |
|
|
|
| [1] |
LI Jun��ZHANG Ling-ling��ZHAO Gui-zhou��CANG Da-qiang. Pilot practice of direct modification of molten blast furnace slag and preparation of mineral wool fiber[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 99-103. |
| [2] |
XU Ren-ze��ZHANG Jian-liang��ZHANG He-shun��LIU Chang-jiang�� FAN Xiao-yue��WANG Zhi-yu. Influence of TiO2 on properties of Jingtang blast furnace slag and thermodynamic analysis[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 104-108. |
| [3] |
JIANG Zhou-hua��ZHANG Xin-fa��LIU Fu-bin��GONG Wei. Harmful impurities control of raw material used in Ni-based superalloy production[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 1-10. |
| [4] |
SONG Guang-yi��YANG Quan��WANG Xiao-chen��ZHANG Xi-bang�� WANG Feng-mei��WANG Qiu-na. Work roll wear law for hot strip temper mill[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 54-59. |
| [5] |
WANG Bing-xing��XIONG Lei��ZHANG Tian��WANG Zhao-dong��WANG Guo-dong. Influence on deformation permeability of plate by controlled rolling process with inter-pass water cooling technology[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 60-65. |
| [6] |
YU Hui��ZHAI Jian-wei��ZHANG Chao-fan��LIU Shuai-shuai��LIU Li-gang. Microstructures and properties of nuclear carbon manganese steels P280GH after accelerated aging[J]. Chinese Journal of Iron and Steel, 2017, 52(9): 66-72. |
|
|
|
|
2015, Vol. 22 