| Effect of Solution Annealing Temperature on Pitting Behavior of Duplex Stainless Steel 2204 in Chloride Solutions |
| Liang HE1,2,Yan- jun GUO1,Xia- yu WU1,Yi- ming JIANG1,Jin LI1 |
1. Department of Materials Science, Fudan University, Shanghai 200433, China
2. School of Materials Engineering, Shanghai University of Engineering Science, Shanghai 201620, China |
|
|
|
|
Abstract The effect of solution annealing temperature ranging from 950 to 1200 �� on the microstructure and corrosion performance of duplex stainless steel (DSS) 2204 were investigated. The proportion of the ferrite phase increased while the austenite phase decreased and the ferrite stabilizing elements diluted in the ferrite phase with the increase of annealing temperature. The critical pitting temperature (CPT) of specimens annealed at 1000 �� was higher than those annealed at 950 ��, whereas further increasing the annealing temperature to 1200 �� decreased the CPT. The pitting initiation sites were observed in the austenite phase, at the boundary of ferrite/austenite phase and inside the ferrite phase for specimens annealed at 950, 1000 �� and exceeding 1100 ��, respectively. The evolution trend of the CPT and the pit initiation site were analyzed by the pitting resistance equivalent number.
|
|
Received: 06 May 2015
Published: 14 April 2016
|
| Fund:National Natural Science Foundation of China;National Natural Science Foundation of China;National Key Technology R&D Program;Doctoral Fund of the Ministry of Education |
|
|
|
| [1] |
Zhi-qiang Wei,Xiang-ru Chen*,Hong-gang Zhong,Qi-jie Zhai,Gang Wang. Hot tearing susceptibility of Fe-20.96Cr-2.13Ni-0.15N-4.76Mn-0.01Mo duplex stainless steel[J]. Chinese Journal of Iron and Steel, 2017, 24(4): 421-425. |
| [2] |
Zhi-gang Song*,Han Feng,Shao��mei Hu. Development of Chinese duplex stainless steel in recent years[J]. Chinese Journal of Iron and Steel, 2017, 24(2): 121-130. |
| [3] |
Ming MA,Hua DING,Zheng-you TANG,Jing-wei ZHAO,Zhou-hua JIANG,Guang-wei FAN. Effects of Temperature and Strain Rate on Flow Behavior and Microstructural Evolution of Super Duplex Stainless Steel under Hot Deformation[J]. Chinese Journal of Iron and Steel, 2016, 23(3): 244-252. |
| [4] |
Li-cong AN,Jing CAO,Lin-cai WU,Hong-huan MAO,Yi-tao YANG. Effects of Mo and Mn on Pitting Behavior of Duplex Stainless Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(12): 1333-1341. |
| [5] |
Qi SUN,,Jian WANG,,Hua-bing LI,Yue LI,,Ya-di HU,,Jin-gang BAI,Pei-de HAN,. Chi Phase after Short-term Aging and Corrosion Behavior in 2205 Duplex Stainless Steel[J]. Chinese Journal of Iron and Steel, 2016, 23(10): 1071-1079. |
| [6] |
Teng ZHANG,Xiao-min LIN,Hui-jun YANG,Yong LIU,Yong-sheng WANG,Jun-wei QIAO. Tribological Properties of a Dendrite-reinforced Ti-based Metallic Glass Matrix Composite under Different Conditions[J]. Chinese Journal of Iron and Steel, 2016, 23(1): 57-63. |
|
|
|
|
2016, Vol. 23 