| Precipitation and Solid Solution of Titanium Carbonitride Inclusions in Hypereutectoid Tire Cord Steel |
| Chen- fan YU,Zheng- liang XUE,Wu- tao JIN |
| The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology,Wuhan 430081, Hubei, China |
|
|
|
|
Abstract The properties of titanium carbonitride Ti(CxN1-x) inclusions precipitated during solidification of tire cord steels and the thermodynamic conditions for their decomposition and solid solution during billet heating were investigated using a thermodynamics method. The solid solution of Ti(CxN1-x) inclusions during high- temperature heating was also studied experimentally. The results revealed that: (1) the higher the content of carbon in the tire cord steel is, the greater the value of x in the Ti(CxN1-x) inclusions is; (2) the higher the content of carbon in the tire cord steel is, the earlier the Ti(CxN1-x) inclusions precipitated during the solidification process and the lower the solidification front temperature is during precipitation; (3) when an 82A steel sample was heated to 1087 ��, the Ti(CxN1-x) inclusions possess the thermodynamic conditions of decomposition and solid solution; and (4) when 82A samples were heated to 1150 and 1250 ��, the total number of Ti(CxN1-x) inclusions larger than 5 ��m in diameter decreased by 55. 0% and 70. 3%, respectively. In addition, although smaller inclusions with diameter less than 2 ��m continued to decompose when the sample was heated at 1250 �� for 2 h and then cooled to 1000 �� in the furnace, the number of inclusions larger than 5 ��m in diameter increased.
|
|
Received: 04 February 2015
Published: 14 April 2016
|
| Fund:The evolution and control ofTitanium inclusion in high strength tire cord steel |
|
Corresponding Authors:
XUE Zheng-Liang
E-mail: xuezhengliang@wust.edu.cn
|
|
|
|
| [1] |
Cai-xia WANG,Jian YANG,,Sha LIU,Xiao-lei XING,Ji-bo WANG,Xue-jun REN,Qing-xiang YANG. Solid Solute Regularity of La Atom in ��-Fe Supercell by First-principles[J]. Chinese Journal of Iron and Steel, 2016, 23(11): 1213-1218. |
| [2] |
WANG Guang-en,WANG Yu,XIE Bing,LI Xin-sheng,GUO Xu,LI Xiao-jun. Effects of Oxides Contents in Vanadium Slag on Corrosion Mechanism of MgO-C Bricks[J]. Chinese Journal of Iron and Steel, 2012, 19(10): 36-42. |
| [3] |
ZHANG Jian��fu;TU Yi��fan;XU Jin;ZHANG Jian��sheng;ZHANG Jing��lin. Effect of Solid Solution Treatment on Microstructure of Fe��Ni Based High Strength Low Thermal Expansion Alloy[J]. Chinese Journal of Iron and Steel, 2008, 15(1): 75-0. |
| [4] |
REN Hui��ping;WANG Hai��yan;LIU Zong��chang;AN Zhi��guo. Nanometer Stripe Microstructure of Supersaturated Solid Solution in Fe��Cu Alloy[J]. Chinese Journal of Iron and Steel, 2007, 14(1): 64-0. |
|
|
|
|
2016, Vol. 23 