| Effects of Solution Depletion and Segregation Oxidation on Morphology of Modified 310 Austenitic Stainless Steel |
| Hong- ying SUN1,Qiang HE1,Zhang- jian ZHOU2,Man WANG2,Guang- ming ZHANG2,Shao- fu LI2 |
1. Key Laboratory of Key Functional Parts of Machine, Anyang Institute of Technology, Anyang 455002,Henan, China
2. School of Materials Science and Engineering, University of Science and Technology Beijing, Beijing 100083, China |
|
|
|
|
Abstract The oxidation morphologies of modified 310 steel exposed in 900 and 1100 �� air were investigated. A double layer morphology consisting of a (Cr,Mn)- rich outer layer and a fine Cr- rich inner layer was formed at 900 ��. It was related to the breakaway oxidation induced by the Cr- depletion and the Mn- segregation in inner layer. Some Cr- rich oxides with amorphous state were formed along grain boundaries. And some new finer oxide grains, voids and Cr- rich precipitates were observed in spallation areas at 1100 ��. Correspondingly, the oxidation kinetic curve dropped with the spallation of scale and increased with the formation of some new oxide grains. It was caused by segregation of Cr and the transformation of oxides from Cr2O3 to the volatile oxides at elevated temperature. XRD analysis showed that the precipitates were mainly composed of CrO3. Segregation and depletion for solutions were also discussed by oxidation diffusion mechanisms.
|
|
Received: 14 January 2015
Published: 14 April 2016
|
| Fund:Natural Science Foundation of China |
|
Corresponding Authors:
Sun Hongying
E-mail: shysun029@163.com
|
|
|
|
| [1] |
Yu-cheng Lei,,*,Xiao-kai Guo,Hong-xia Chang,Tian-qing Li,,Qiang Zhu,Gang Chen, Long-ren Xiao. Cavitation erosion behavior of CLAM steel weld joint in liquid lead-bismuth eutectic alloy[J]. Chinese Journal of Iron and Steel, 2017, 24(9): 935-942. |
| [2] |
Zhi-gang Song,En-xiang Pu,. Precipitated phases of superaustenitic stainless steel 654SMO[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 743-749. |
| [3] |
Ying-yi Zhang,Wei Lv,Xue-wei Lv,Chen-guang Bai,Ke-xi Han,Bing Song. Oxidation kinetics of ilmenite concentrate by non-isothermal thermogravimetric analysis[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 678-684. |
| [4] |
Jia-long Tian,,Wei Wang,,Wei Yan,,Zhou-hua Jiang,Yi-yin Shan,,Ke Yang. Microstructure characteristics of segregation zone in 17-4PH stainless steel piston rod[J]. Chinese Journal of Iron and Steel, 2017, 24(7): 718-723. |
| [5] |
Rui Wang,Yan-ping Bao,*,Yi-hong Li,Tai-quan Li,Di Chen. Effect of slag composition on steel cleanliness in interstitial-free steel[J]. Chinese Journal of Iron and Steel, 2017, 24(6): 579-585. |
| [6] |
Yu Xu,,En-gang Wang,,*,Zhuang Li,,An-yuan Deng,. Effects of vertical electromagnetic stirring on grain refinement and macrosegregation control of bearing steel billet in continuous casting[J]. Chinese Journal of Iron and Steel, 2017, 24(5): 483-489. |
|
|
|
|
2016, Vol. 23 