| Electroslag Remelting Withdrawing Technology for Offshore Jack- up Platform Rack Steel Manufacturing Process |
| Xi- min ZANG1,Tian- yu QIU1,Wan- ming LI1,Xin DENG1,Zhou- hua JIANG1,2,Hua SONG3 |
1. School of Material and Metallurgy, University of Science and Technology Liaoning, Anshan 114051,Liaoning, China
2. School of Metallurgy, Northeastern University, Shenyang 110819, Liaoning,China
3. School of Mechanical Engineering and Automation, University of Science and TechnologyLiaoning, Anshan 114051, Liaoning, China |
|
|
|
|
Abstract Offshore jack- up platform rack steel must exhibit high strength and toughness as well as excellent welding properties. A high- quality large ingot is a prerequisite for obtaining a high- performance rough part. The electroslag remelting withdrawing (ESRW) technology using a T- shaped mold and bifilar mode was introduced to replace casting technology. Numerical simulation of the ESRW process was performed to determine the distribution of the temperature and velocity fields and to determine the optimum process for producing rack steels. Several A514Q slab ingots with dimensions of 0. 32 m��1. 40 m��4. 00 m were produced using ESRW technology in an industrial plant. The industrial test indicated that slab ingots produced by the ESRW method exhibited uniform chemical compositions and compact macrostructures. A 115. 4 mm thick plate was produced from the rough ingot after 11 rolling passes. Samples were obtained from different positions in the steel plate to test the mechanical performance and examine the microstructure, and the results revealed that the properties of the steel plate satisfied ASTM standards. The ESRW process improved the tensile strength and toughness of the slab ingot, enabling significant improvements in the anisotropy and low temperature toughness, which are critical for the development of rack steel for offshore platforms.
|
|
Received: 31 March 2015
Published: 14 April 2016
|